Eurostar Staramide R1000EI2 PA66, Impact Modified, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide R1000EI2 PA66, Impact Modified, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide R1000EI2 is an Impact Modified Polyamide 66 Injection Molding Resin (also known as R1000HI010)Information provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.011 - 0.015 cm/cm @Time 86400 sec |
0.011 - 0.015 in/in @Time 24.0 hour |
ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.015 cm/cm @Time 86400 sec |
0.010 - 0.015 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | ISO 527 |
| Elongation at Break | >= 40 % | >= 40 % | ISO 527 |
| Tensile Modulus | 2.20 GPa | 319 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 70.0 MPa | 10200 psi | ISO 178 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 96.0 kJ/m² | 45.7 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 260 - 270 °C | 500 - 518 °F | |
| Zone 2 | 270 - 290 °C | 518 - 554 °F | |
| Zone 3 | 270 - 280 °C | 518 - 536 °F | |
| Melt Temperature | 270 - 280 °C | 518 - 536 °F | |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- PolyOne Elastamax™ XL-2075 Thermoplastic Polyolefin Elastomer (TPO (POE))
- PolyOne Geon™ Vinyl Wire & Cable WJJC310L Polyvinyl Chloride, Flexible (PVC, Flexible)
- Resin Technology Group Fusion 902 Odorless, Non-Frosting Fusion Cyanoacrylate
- SABIC Innovative Plastics LNP Lubricomp UCL24S PPA (Asia Pacific)
- Techmer ES HiFill® PA6/6 GF70 HS L BK 70% Glass Filled
- Eurostar Staramide A24G6K PA66, 30% Glass Fiber Reinforced, Heat stabilized, Injection Molding
- BorsodChem ONGROCLEAN 10 anti-scaling agent
- BASF Elastollan® C-74D Polyester Type Polyurethane Elastomer
- SABIC Innovative Plastics Cycolac® DL100LG ABS (Europe-Africa-Middle East)
- Shakespeare WonderThread® SN-40 ultra soft TEX# 80 Nylon Industrial Sewing Thread
Copyright © lookpolymers.com All Rights Reserved