SABIC Innovative Plastics ULTEM ATX100 PEI+PCE (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI) + PCE |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM ATX100 PEI+PCE (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Higher impact, high flow Polyetherimide blend. ECO Conforming, UL94 HB Listing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 6.0 g/10 min @Load 6.60 kg, Temperature 295 °C |
6.0 g/10 min @Load 14.6 lb, Temperature 563 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 68.0 MPa | 9860 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 80 % | 80 % | Type I, 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 106 MPa | 15400 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 2.53 GPa | 367 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 4.27 J/cm | 8.00 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 20.82 J/cm | 39.00 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C @Thickness 6.40 mm |
315 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 115 °C | 239 °F | UL 746B |
| UL RTI, Mechanical with Impact | 115 °C | 239 °F | UL 746B |
| UL RTI, Mechanical without Impact | 115 °C | 239 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 0.760 mm |
HB @Thickness 0.0299 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A |
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ FR WC 0521-48 R1 RoHS Polypropylene, Unspecified (PP, Unspecified)
- Polimeri Europa Extir® A 7000 AE Expandable Polystyrene, Standard Flame Retardant
- Polykemi AB POLYform POM C M20 AS4 Polyoxymethylene, Antistatic
- A. Schulman POLYBATCH™ White LL8425 MG Concentrate Based In LLDPE
- A. Schulman POLYFORT™ PP 3045
- Covestro Bayblend® ET3036 FR PC/ABS Blend
- Bhansali Engineering Abstron IMG-1115 Glass Reinforced Grade
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 70 PHR N330 (HAF) Filler
- Plastcom SLOVALEN PH 79 GF 20 Polypropylene Homopolymer, 20% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved