Eastman Eastar DN102 PCTG Copolyester  (discontinued **)

Category Polymer , Thermoplastic , Polyester, TP , Polycyclohexylenedimethylene Terephthalate (PCT) , Glycol-Modified PCT (PCTG) Copolyester
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eastman Eastar DN102 PCTG Copolyester  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ISO data as provided by the manufacturer, Eastman Chemical
Physical Properties Metric English Comments
Density 1.23 g/cc
0.0444 lb/in³
Linear Mold Shrinkage, Flow 0.0020 - 0.0050 cm/cm
0.0020 - 0.0050 in/in
Mechanical Properties Metric English Comments
Tensile Strength, Yield 46.0 MPa
6670 psi
50 mm/min
Elongation at Break >= 50 %
>= 50 %
Elongation at Yield 4.4 %
4.4 %
Tensile Modulus 2.09 GPa
303 ksi
1mm/min
Charpy Impact Unnotched NB
NB
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
Charpy Impact, Notched 0.830 J/cm²
3.95 ft-lb/in²
0.480 J/cm²

@Temperature -30.0 °C
 2.28 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 87.0 µm/m-°C

@Temperature 20.0 °C
 48.3 µin/in-°F

@Temperature 68.0 °F
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature 20.0 °C
 38.9 µin/in-°F

@Temperature 68.0 °F
Melting Point 225 °C
437 °F
Deflection Temperature at 0.46 MPa (66 psi) 78.0 °C
172 °F
Deflection Temperature at 1.8 MPa (264 psi) 70.0 °C
158 °F
Vicat Softening Point 83.0 °C
181 °F
Glass Transition Temp, Tg 82.0 °C
180 °F
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
 HB

@Thickness 0.126 in
HB

@Thickness 3.20 mm
 HB

@Thickness 0.126 in
Processing Properties Metric English Comments
Melt Temperature 275 - 295 °C
527 - 563 °F