Eurostar Staramide PF006IX1 PA6, Glass Fiber Filled, Impact Modified, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Filled, Impact Grade |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide PF006IX1 PA6, Glass Fiber Filled, Impact Modified, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide PF006IX1 is an Impact Modified, Glass Fiber Reinforced, Polyamide 6 Injection Molding Resin (also known as Star X R2005-30V)Information provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | on Tensile Bar; E2P method |
| Ash | 30 % @Temperature 650 °C |
30 % @Temperature 1200 °F |
ISO 3451 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 160 MPa | 23200 psi | 5 mm/min; ISO 527 |
| Elongation at Yield | 2.0 - 3.0 % | 2.0 - 3.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 8.00 GPa | 1160 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 200 MPa | 29000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 7.00 GPa | 1020 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
80x10x4; ISO 180/1A |
| 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 75.0 kJ/m² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1U |
| 75.0 kJ/m² @Temperature -30.0 °C |
35.7 ft-lb/in² @Temperature -22.0 °F |
80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |
| Zone 2 | 240 - 250 °C | 464 - 482 °F | |
| Zone 3 | 240 - 260 °C | 464 - 500 °F | |
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- PolyOne Bergamid™ B70 W25 Polyamide 6 (Nylon 6)
- PolyOne Edgetek® PF-05GF/000 FR MR Polysulfone (PSU)
- DuPont Performance Polymers Zytel® 103HSL BKB080 Nylon 66 (Unverified Data**)
- Huntsman HY 9130 Polyamide
- Daikin POLYFLON MG-1241 PTFE 20% Glass Fiber and 5% Graphite Filled Molding Powder
- ExxonMobil Oppalyte™ 36MO747 OPP Film
- Esstech X-947-7446 Trimethylolpropane Trimethacrylate, C18H26O6
- Dow Corning 1418 Fluid
- Chevron Phillips EA3025 Crystal Polystyrene (discontinued **)
- Raschig Group 5567 DAP Diallyl Phthalate (DAP), Cast, Mineral Filler
Copyright © lookpolymers.com All Rights Reserved