Eurostar Staramide BG3 PA6, 15% Glass Filled, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide BG3 PA6, 15% Glass Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
BG3 is a 15% Glass Fiber Reinforced Polyamide 6 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 8.0 % @Temperature 23.0 °C |
8.0 % @Temperature 73.4 °F |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0045 - 0.0085 cm/cm | 0.0045 - 0.0085 in/in | on Tensile Bar; ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 110 | 110 | ISO 2039-2 |
| Tensile Strength at Break | 125 MPa | 18100 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.5 % | 3.5 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 5.80 GPa | 841 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 180 MPa | 26100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.75 GPa | 689 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
80x10x4; ISO 180/1U |
| 40.0 kJ/m² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1U | |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | Edgew 80x10x4 sp=62; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
27.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature 23.0 - 60.0 °C |
55.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Af |
| Vicat Softening Point | 206 °C | 403 °F | B/120; ISO 306 |
| UL RTI, Electrical | 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
|
| 65.0 °C @Thickness 1.50 mm |
149 °F @Thickness 0.0591 in |
||
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
|
| 65.0 °C @Thickness 1.50 mm |
149 °F @Thickness 0.0591 in |
||
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
|
| 65.0 °C @Thickness 1.50 mm |
149 °F @Thickness 0.0591 in |
||
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
||
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
IEC 60695-11-10 |
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC 60695-11-10 | |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
IEC 60695-11-10 | |
| Oxygen Index | 24 % | 24 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.4 @Frequency 1.00e+6 Hz |
3.4 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.6 @Frequency 50.0 - 60.0 Hz |
3.6 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 20.0 kV/mm @Thickness 3.20 mm |
508 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0061 @Frequency 50.0 - 60.0 Hz |
0.0061 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.016 @Frequency 1.00e+6 Hz |
0.016 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 450 V | 450 V | M; IEC 60112 |
| 550 V | 550 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 230 - 240 °C | 446 - 464 °F | Zone 1 |
| Middle Barrel Temperature | 240 - 250 °C | 464 - 482 °F | Zone 2 |
| Front Barrel Temperature | 240 - 270 °C | 464 - 518 °F | Zone 3 |
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 75.0 - 85.0 °C | 167 - 185 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- PolyOne LubriOne™ SF2-30CF/15T Natural Polyphenylene Sulfide (PPS)
- Flint Hills P4C6S-193A Homopolymer Polypropylene
- Garlock GYLON® 3545 Layered Microcellular PTFE Gasketing
- Glastic 1120 Corrosion-Resistant Panels
- Kraton® D1116 E (SBS) Radial Triblock Copolymer
- Lucent Polymers CPP-230 Polypropylene, 30% Calcium Carbonate Filled, Impact Modified
- Greene Tweed Arlon® 1263 PEEK, Carbon Filled
- Elektro-Isola G-Etronax EP S Epoxy, Glass Fabric Reinforcement, Green, Sheets
- 3M 12038 Black 3/8" (9.5 mm) Polyurethane Foam
Copyright © lookpolymers.com All Rights Reserved