SABIC Innovative Plastics LNP Thermocomp MH0500A PP (Asia Pacific)
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp MH0500A PP (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* MH0500A is a compound based on Polypropylene resin. Added features of this material include: High Specific Gravity.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 5.00 g/cc | 0.181 lb/in³ | ASTM D 792 |
| 5.00 g/cc | 0.181 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.050 % | 0.050 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.011 - 0.013 cm/cm @Time 86400 sec |
0.011 - 0.013 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.011 - 0.013 cm/cm @Time 86400 sec |
0.011 - 0.013 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.011 - 0.013 cm/cm @Time 86400 sec |
0.011 - 0.013 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.011 - 0.013 cm/cm @Time 86400 sec |
0.011 - 0.013 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 9.00 MPa | 1310 psi | ASTM D 638 |
| 12.0 MPa | 1740 psi | ISO 527 | |
| Tensile Strength, Yield | 13.0 MPa | 1890 psi | ISO 527 |
| Elongation at Break | 3.9 % | 3.9 % | ISO 527 |
| 5.5 % | 5.5 % | ASTM D 638 | |
| Elongation at Yield | 1.7 % | 1.7 % | ISO 527 |
| Tensile Modulus | 2.62 GPa | 380 ksi | 50 mm/min; ASTM D 638 |
| 2.80 GPa | 406 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 27.0 MPa | 3920 psi | ASTM D 790 |
| 31.0 MPa | 4500 psi | ISO 178 | |
| Flexural Modulus | 5.49 GPa | 796 ksi | ISO 178 |
| 5.55 GPa | 805 ksi | ASTM D 790 | |
| Izod Impact, Notched | 0.420 J/cm @Temperature 23.0 °C |
0.787 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 0.960 J/cm @Temperature 23.0 °C |
1.80 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 8.00 kJ/m² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 6.00 J | 4.43 ft-lb | Multiaxial Impact; ISO 6603 |
| 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 86.0 °C @Thickness 3.20 mm |
187 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 3413HF PC (Asia Pacific)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with TCP Plasticizer
- Hyosung Topilene J440 PP
- Borealis MG9621S Polyethylene
- Universal Wire Works 61 Nickel Alloy Welding Wire
- EMS-Grivory Grivory® GV-2H black PA*-GF20
- Diamond Polymers DIAMALOY 761 ABS/PC Alloy, Non-Halogen Flame Retardant with 5% PTFE
- Dura-Bar 60-40-18 Continuously Cast Ductile Iron Bar Stock ASTM A536, 4018
- Huntsman PE2060 Injection Molding Polyethylene (discontinued **)
- Plastcom SLOVASTER® B GB 40 PBT reinforced with glass beads
Copyright © lookpolymers.com All Rights Reserved