Eurostar Staramide AG10 PA66, 50% Glass Filled, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide AG10 PA66, 50% Glass Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AG10 is a 50% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.700 % @Temperature 23.0 °C |
0.700 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | 2.5 % @Temperature 23.0 °C |
2.5 % @Temperature 73.4 °F |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0025 cm/cm | 0.0010 - 0.0025 in/in | on Tensile Bar; ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 114 | 114 | ISO 2039-2 |
| Tensile Strength at Break | 210 MPa | 30500 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 14.8 GPa | 2150 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 310 MPa | 45000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 13.8 GPa | 2000 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
80x10x4; ISO 180/1A |
| 13.0 kJ/m² @Temperature -40.0 °C |
6.19 ft-lb/in² @Temperature -40.0 °F |
80x10x4; ISO 180/1A | |
| 14.0 kJ/m² @Temperature -20.0 °C |
6.66 ft-lb/in² @Temperature -4.00 °F |
80x10x4; ISO 180/1A | |
| 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1A | |
| Charpy Impact Unnotched | 14.0 J/cm² | 66.6 ft-lb/in² | Edgew 80x10x4 sp=62; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 19.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
10.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 71.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
39.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 262 °C | 504 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 258 °C | 496 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Af |
| Vicat Softening Point | 260 °C | 500 °F | B/120; ISO 306 |
| 260 °C | 500 °F | B/50; ISO 306 | |
| UL RTI, Electrical | 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
|
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
|
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
|
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
||
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
IEC 60695-11-10 |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
IEC 60695-11-10 | |
| Flame Spread | 2.00 mm/min @Thickness 3.00 mm |
0.0787 in/min @Thickness 0.118 in |
FMVSS Buring Speed |
| 6.00 mm/min @Thickness 2.00 mm |
0.236 in/min @Thickness 0.0787 in |
FMVSS Buring Speed | |
| Oxygen Index | 27 % | 27 % | ISO 4589 |
| Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.4 @Frequency 50.0 - 60.0 Hz |
3.4 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 19.0 kV/mm @Thickness 3.20 mm |
483 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0068 @Frequency 50.0 - 60.0 Hz |
0.0068 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 350 V | 350 V | M; IEC 60112 |
| 500 V | 500 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 280 °C | 500 - 536 °F | Zone 1 |
| Middle Barrel Temperature | 270 - 280 °C | 518 - 536 °F | Zone 2 |
| Front Barrel Temperature | 270 - 290 °C | 518 - 554 °F | Zone 3 |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 75.0 - 85.0 °C | 167 - 185 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |
| Moisture Content | 0.20 % | 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Potable Water | ACS WRAS | |
| UL f1 | f1 |
Users viewing this material also viewed the following:
- Nitriflex Nitrigum 50 G Styrene Butadiene Rubber
- Taiwan Sheen Soon Sheenthane® AH-500 TPU for Hotmelt Adhesive
- A. Schulman POLYBATCH™ White LL8575 AP Concentrate Based In LLDPE
- A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin
- DSM Akulon® K224-HG7 (Cond.) 35% Glass Reinforced Nylon 6 (North America)
- Fainplast Compounds GS 46/T Flexible PVC, Injection Molding for Footwear
- Asahi Kasei Tenac® LA543 Homopolymer Acetal Resin
- E-Polymers SEPAZ® V330FR 30% Glass Fiber Reinforced Flame Retardant PPA
- Addiplast Addinyl B2 V40 Nylon 6, 40% Glass Filled
Copyright © lookpolymers.com All Rights Reserved