Polykemi AB POLYfill PP HIP16020FCF Polypropylene, Fast Cycle
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | Polykemi AB |
| Trade Name | POLYfill |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYfill PP HIP16020FCF Polypropylene, Fast Cycle.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Filler Content | 20 % | 20 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | With Flow; ISO 2577 |
| 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 16 g/10 min @Load 2.16 kg, Temperature 230 °C |
16 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 67 @Time 15.0 sec |
67 @Time 0.00417 hour |
ASTM D2240 |
| Tensile Strength at Break | <= 30.0 MPa | <= 4350 psi | ISO/R527 |
| Elongation at Break | 44 % | 44 % | ISO/R527 |
| Flexural Strength | <= 46.0 MPa | <= 6670 psi | ISO 178 |
| Flexural Modulus | 2.60 GPa @Temperature 23.0 °C |
377 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature -20.0 °C |
0.952 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 0.400 J/cm² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Glow Wire Test | 750 °C @Thickness 2.00 mm |
1380 °F @Thickness 0.0787 in |
IEC 695-2-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 205 - 260 °C | 401 - 500 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | in circulation dryer |
| 2 - 4 hour | 2 - 4 hour | in desiccant air dryer | |
| Injection Pressure | 40.0 - 110 MPa | 5800 - 16000 psi | |
| Back Pressure | 1.00 - 2.00 MPa | 145 - 290 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | 20-40 | % of injection pressure |
| Injection Speed () | High |
Users viewing this material also viewed the following:
- ExxonMobil Escorene® LD-708 EVA Film Resin (discontinued **)
- Lushan M-1 Adhesive Resin for Barrier Container and Tube
- Solvay Technyl® A218 Heat Stabilized Nylon 66
- SABIC Innovative Plastics LNP THERMOCOMP QC006I PA 6/10
- Styron EMERGEâ„¢ 4330-22 Polycarbonate
- Samsung Cheil Industries Starex® WX-9120 ASA, Unreinforced
- Denka REOMER G G8082 Thermoplastic Elastomer, For Injection Molding
- Fainplast Compounds Ethylplus 621 HD Polyethylene Cable Compound
- Aclo Accucomp ABS ABS803L Medium Impact Grade
- Westlake EMAC® SP 1205 Ethylene-Methyl Acrylate Copolymer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved