Eurostar Staramide A28N PA66, Nucleated, Injection Molding
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Nucleated |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide A28N PA66, Nucleated, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide A28K is an Unreinforced and Heat Stabilized, Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Moisture Absorption | 2.00 % @Temperature 23.0 °C |
2.00 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | 8.5 % @Temperature 23.0 °C |
8.5 % @Temperature 73.4 °F |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.016 - 0.020 cm/cm | 0.016 - 0.020 in/in | on Tensile Bar; E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 118 | 118 | ISO 2039-2 |
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | 50 mm/min; ISO 527 |
| Elongation at Break | >= 20 % | >= 20 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 3.8 % | 3.8 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 3.00 GPa | 435 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 105 MPa | 15200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.80 GPa | 406 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
80x10x4; ISO 180/1A |
| 3.00 kJ/m² @Temperature -40.0 °C |
1.43 ft-lb/in² @Temperature -40.0 °F |
80x10x4; ISO 180/1A | |
| 4.00 kJ/m² @Temperature -20.0 °C |
1.90 ft-lb/in² @Temperature -4.00 °F |
80x10x4; ISO 180/1A | |
| 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1A | |
| Charpy Impact Unnotched | >= 10.0 J/cm² @Temperature -30.0 °C |
>= 47.6 ft-lb/in² @Temperature -22.0 °F |
Edgew 80x10x4 sp=62; ISO 179/1eU |
| >= 27.0 J/cm² @Temperature 23.0 °C |
>= 128 ft-lb/in² @Temperature 73.4 °F |
Edgew 80x10x4 sp=62; ISO 179/1eU | |
| Charpy Impact, Notched | 0.300 J/cm² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
Edgew 80x10x4 sp=62; ISO 179/1eA |
| 0.500 J/cm² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
Edgew 80x10x4 sp=62; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.290 W/m-K | 2.01 BTU-in/hr-ft²-°F | ISO 8302 |
| Hot Ball Pressure Test | 123 - 127 °C | 253 - 261 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Vicat Softening Point | 240 °C | 464 °F | B/120; ISO 306 |
| 243 °C | 469 °F | B/50; ISO 306 | |
| UL RTI, Electrical | 65.0 °C | 149 °F | |
| UL RTI, Mechanical with Impact | 65.0 °C | 149 °F | |
| UL RTI, Mechanical without Impact | 65.0 °C | 149 °F | |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
|
| Oxygen Index | 26 % | 26 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | ROA; IEC 60093 |
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.2 @Frequency 50.0 - 60.0 Hz |
3.2 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 16.0 kV/mm @Thickness 3.20 mm |
406 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0055 @Frequency 50.0 - 60.0 Hz |
0.0055 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.017 @Frequency 1.00e+6 Hz |
0.017 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| 600 V | 600 V | M; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 260 - 270 °C | 500 - 518 °F | |
| Zone 2 | 270 - 280 °C | 518 - 536 °F | |
| Zone 3 | 270 - 290 °C | 518 - 554 °F | |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Pau Tai Unistab BC-541 Mixed Metal Liquid Stabilizer for PVC Cadmium/Barium/Zinc Self-Lubricating
- Overview of materials for Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler
- Indium Corp. Indalloy 63 Bismuth Solder Alloy
- Lucas-Milhaupt BRAZE 300 Silver Based Cadmium Free Filler Metal
- Lucent Polymers GPB-130 Polybutylene Terephthalate, 30% Glass Fiber Reinforced
- SABIC Innovative Plastics LNP THERMOCOMP UCF26AS PPA
- Lubrizol ESTANE® 58138 Ester Based Thermoplastic Polyurethane
- Diamond Polymers ASA TW-20
- Chosun Refractories APC-2 Special Mortar
- 3M Novec™ 1720 Electronic Grade Coating
Copyright © lookpolymers.com All Rights Reserved