- A. Schulman POLYFORT™ FPP 809 Talc Filled Homopolymer Polypropylene
A. Schulman POLYFORT™ FPP 809 Talc Filled Homopolymer Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman POLYFORT™ FPP 809 Talc Filled Homopolymer Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DescriptionPolyfort® FPP 809 is a 40% talc-filled homopolymer polypropylene.Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.56 g/cc | 1.56 g/cc | ASTM D792 |
| Melt Flow | 6.0 - 10 g/10 min @Temperature 230 °C |
6.0 - 10 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 97 | 97 | ASTM D785 |
| Tensile Strength, Yield | 29.5 MPa | 4280 psi | ASTM D638 |
| Flexural Modulus | 3.585 GPa | 520.0 ksi | ASTM D790 |
| Izod Impact, Notched | 0.270 J/cm | 0.506 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.68 J/cm | 5.02 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66/6 HI/1 PA66/6, improved strength
- Paratherm Corporation Paratherm™ CR Heat Transfer Fluid
- Eastman Eastapak 7352 PET (discontinued **)
- Zircar Zirconia ZYP-30 Zirconia Powder
- A. Schulman POLYFORT™ FXP 1227U UV Stable Copolymer Polypropylene
- A. Schulman FORMION™ FI 131E Adhesive, Extrusion Grade
- Dow Corning SILASTIC® 3496 MOULD MAKING BASE & 96 CURING AGENT
- Eurostar Staramide P1000EI3 PA6, Impact Modified, Injection Molded
- Aremco HiE-Coat™ 840-C High Emissivity Coating, Inorganic-Ceramic Filled
Copyright © lookpolymers.com All Rights Reserved