- HOME
- POLYMER SEARCH
- Thermoplastic
- Polysulfone (PSU)
- SABIC Innovative Plastics LNP THERMOCOMP GX05482 PSU
SABIC Innovative Plastics LNP THERMOCOMP GX05482 PSU
| Category | Polymer , Thermoplastic , Polysulfone (PSU) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP GX05482 PSU.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* GX05482 is a compound based on Polysulfone resin containing 30% Glass Fiber. Added features of this material include: Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.51 g/cc | 1.51 g/cc | ASTM D792 |
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 |
| 1.52 g/cc | 0.0549 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.160 % | 0.160 % | 50% RH, 24 hrs; ASTM D570 |
| 0.250 % | 0.250 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 104 MPa | 15100 psi | 5 mm/min; ISO 527 |
| 115 MPa | 16700 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 8.72 GPa | 1260 ksi | 1 mm/min; ISO 527 |
| 9.14 GPa | 1330 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 162 MPa | 23500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 163 MPa | 23600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 8.05 GPa | 1170 ksi | 2 mm/min; ISO 178 |
| 8.66 GPa | 1260 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.610 J/cm | 1.14 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.51 J/cm | 8.45 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 27.0 kJ/m² | 12.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 12.0 J @Temperature 23.0 °C |
8.85 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 46.6 µm/m-°C @Temperature -30.0 - 30.0 °C |
25.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 40.6 µm/m-°C @Temperature -30.0 - 30.0 °C |
22.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 175 °C @Thickness 3.20 mm |
347 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 171 °C | 340 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 171 °C @Thickness 3.20 mm |
340 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- RheTech Products G40P100-00 40% Glass Fiber Reinforced Polypropylene, Natural
- PolyOne Edgetek® PS-30CF/000 Polybutylene Terephthalate (PBT), Carbon Fiber Reinforced (discontinued **)
- Ferro EG 0024 Specialty Glass
- Ineos N05G-00 Polypropylene Impact Copolymer
- Zylog Hipolyene® 5131 SX-5 Thermoplastic Polyolefin & PP Compound
- A. Schulman PP 3052X-01 Polypropylene Impact Resistant Copolymer
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 60 PHR Non-Black, Aerosil 200
- Covestro Makrolon® 2805 Polycarbonate, Injection Grade
- Covestro Makrolon® 9415(Z) Polycarbonate
- Arkema Group EVATANE® 28-03 Copolymer Ethylene - Vinyl Acetate
Copyright © lookpolymers.com All Rights Reserved