DuPont Performance Polymers Zytel® ST811HS BK038 Nylon 6 (Unverified Data**)

Category	Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer	DuPont Performance Polymers
Trade Name	Zytel®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Zytel® ST811HS BK038 Nylon 6 (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Zytel® ST811HS BK038 is a flexible, non-plasticized, black Super Tough nylon 6 resin developed for extrusion and injection molding applications such as cable and rope jacketing, hose inner cores and molded fasteners and ski binding parts.Information provided by DuPont

Physical Properties	Metric	English	Comments
Density	1.05 g/cc	0.0379 lb/in³	DAM; ISO 1183
Linear Mold Shrinkage, Flow	0.0090 cm/cm @Thickness 2.00 mm	0.0090 in/in @Thickness 0.0787 in	DAM; ISO 294-4
Linear Mold Shrinkage, Transverse	0.014 cm/cm @Thickness 2.00 mm	0.014 in/in @Thickness 0.0787 in	DAM; ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	44.0 MPa @Temperature 23.0 °C	6380 psi @Temperature 73.4 °F	DAM; 50mm/min; ISO 527
Elongation at Break	200 % @Temperature 23.0 °C	200 % @Temperature 73.4 °F	DAM; ISO 527
	230 % @Temperature 23.0 °C	230 % @Temperature 73.4 °F	DAM; 50mm/min; ISO 527
Tensile Modulus	0.850 GPa @Temperature 23.0 °C	123 ksi @Temperature 73.4 °F	DAM; ISO 527
Flexural Modulus	0.850 GPa @Temperature 23.0 °C	123 ksi @Temperature 73.4 °F	DAM; ISO 178
Izod Impact, Notched (ISO)	13.0 kJ/m² @Temperature -40.0 °C	6.19 ft-lb/in² @Temperature -40.0 °F	DAM; ISO 180/1A
	36.0 kJ/m² @Temperature -20.0 °C	17.1 ft-lb/in² @Temperature -4.00 °F	DAM; ISO 180/1A
	65.0 kJ/m² @Temperature 23.0 °C	30.9 ft-lb/in² @Temperature 73.4 °F	DAM; ISO 180/1A
Izod Impact, Unnotched (ISO)	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	DAM; ISO 180/1U
Charpy Impact Unnotched	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	DAM; ISO 179/1eU
Charpy Impact, Notched	1.20 J/cm² @Temperature -40.0 °C	5.71 ft-lb/in² @Temperature -40.0 °F	DAM; ISO 179/1eA
	8.00 J/cm² @Temperature 23.0 °C	38.1 ft-lb/in² @Temperature 73.4 °F	DAM; ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	130 µm/m-°C @Temperature 23.0 - 55.0 °C	72.2 µin/in-°F @Temperature 73.4 - 131 °F	DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow	140 µm/m-°C @Temperature 23.0 - 55.0 °C	77.8 µin/in-°F @Temperature 73.4 - 131 °F	DAM; ISO 11359-1/-2
Melting Point	218 °C	424 °F	DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	85.0 °C	185 °F	DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	40.0 °C	104 °F	DAM; ISO 75-1/-2

Processing Properties	Metric	English	Comments
Melt Temperature	240 °C	464 °F	DAM; optimum; Extrusion
	235 - 250 °C	455 - 482 °F	DAM; Extrusion
	260 - 280 °C	500 - 536 °F	DAM; Injection Molding
	270 °C	518 °F	DAM; optimum; Injection Molding
Mold Temperature	70.0 °C	158 °F	DAM; Optimum; Injection Molding
	50.0 - 90.0 °C	122 - 194 °F	DAM; Injection Molding
Drying Temperature	80.0 °C	176 °F	DAM; Extrusion
	80.0 °C	176 °F	DAM; Injection Molding
Dry Time	2.00 - 4.00 hour	2.00 - 4.00 hour	DAM; Dehumidified Dryer; Injection Molding
	4.00 - 6.00 hour	4.00 - 6.00 hour	DAM; Dehumidified Dryer; Extrusion
Moisture Content	<= 0.060 %	<= 0.060 %	DAM; Extrusion
	<= 0.060 %	<= 0.060 %	DAM; Injection Molding

Descriptive Properties	Value	Comments
Additive	Carbon Black
	Heat Stabilizer
	Impact Modifier, Rubber
Appearance	Natural Color
Drying Recommended	Yes, if moisture content of resin exceeds recommended level
Features	Elongation, Good
	Flexibility, Good
	Heat Aging Resistance, Good
	Heat Stabilized
	Impact Modified
	Impact Resistance, Good
	Lubricated
	Toughness, Good
Forms	Pellets
Generic	Nylon 6
Material Status	Current
Part Marking Code	>PA6-HI<	ISO 11469
Processing Method	Extrusion
Product Category	Extrusion Resins
	Toughened Resins
Region Available - Global	Yes
Resin Identification	PA6-HI	ISO 1043
RoHS Compliance	Contact Manufacturer
Uses	Cable Jacketing
	Liners