DuPont Performance Polymers Zytel® FG50 NC010 Nylon 66 (Unverified Data**)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | DuPont Performance Polymers |
| Trade Name | Zytel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Zytel® FG50 NC010 Nylon 66
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unreinforced High Viscosity Polyamide 66 with Developed for Food Contact Applications Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | DAM; ISO 1183 |
| Water Absorption | 8.5 % @Thickness 2.00 mm |
8.5 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 |
| Moisture Absorption | 2.70 % @Thickness 2.00 mm |
2.70 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 |
| Viscosity Test | 300 cm³/g | 300 cm³/g | DAM; ISO 307 1157 1628 |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm | 0.015 in/in | DAM; ISO 294-4 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | 50%RH; ISO 527-1/-2 |
| 82.0 MPa | 11900 psi | DAM; ISO 527-1/-2 | |
| Elongation at Break | >= 50 % | >= 50 % | DAM; Nominal; ISO 527-1/-2 |
| >= 50 % | >= 50 % | 50%RH; Nominal; ISO 527-1/-2 | |
| Elongation at Yield | 4.5 % | 4.5 % | DAM; ISO 527-1/-2 |
| 28 % | 28 % | 50%RH; ISO 527-1/-2 | |
| Tensile Modulus | 1.20 GPa | 174 ksi | 50%RH; ISO 527-1/-2 |
| 3.00 GPa | 435 ksi | DAM; ISO 527-1/-2 | |
| Charpy Impact Unnotched | NB | NB | DAM; ISO 179/1eU |
| NB | NB | 50%RH; ISO 179/1eU | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
DAM; ISO 179/1eU | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
50%RH; ISO 179/1eU | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | DAM; ISO 179/1eA |
| 2.90 J/cm² | 13.8 ft-lb/in² | 50%RH; ISO 179/1eA | |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eA | |
| 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 100 µm/m-°C | 55.6 µin/in-°F | DAM; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | DAM; ISO 11359-1/-2 |
| Melting Point | 263 °C | 505 °F | DAM; 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | DAM; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | DAM; ISO 75-1/-2 |
| Vicat Softening Point | 245 °C | 473 °F | DAM; 50°C/h 50N; ISO 306 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Delivery Form | Pellets | |
| Processing | Casting | |
| Coatable | ||
| Film Extrusion | ||
| Injection Moulding | ||
| Other Extrusion | ||
| Profile Extrusion | ||
| Sheet Extrusion | ||
| Regional Availability | Europe | |
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- LG Chemical HP PMMA
- Iran Petrochemical (PCC) 2101TN47 Low Density Polyethylene
- Techmer ES HiFill® PBT WM35 X
- Styron DL 460E SB Latex
- A. Schulman POLYBATCH™ Red 5670 Concentrate Based In Polyethylene
- Diamond Polymers NPP 808 C4 TDS Polycarbonate Alloy
- CLAL-MSX NICLAFOR® 1000 TH2 Quenched/Precipitation Heat Treated, Drawn Copper Alloy
- BASF Ultrason S 6010 PSU
- Arlon R36812T010 0.010" Cured Silicone Rubber with Laminated ETFE Film Substrate
Copyright © lookpolymers.com All Rights Reserved