Permabond HL126 Anaerobic Threadlocker
| Category | Polymer , Adhesive , Thermoset , Acrylic/Cyanoacrylate Adhesive |
| Manufacturer | Permabond |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Permabond HL126 Anaerobic Threadlocker.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PERMABOND® HL126 Threadlocker is a water thin product for locking pre-assembled parts through wicking action. PERMABOND® HL126 Threadlocker prevents vibration loosening. Because of the low viscosity an additional use is the sealing of weld porosity; the uncured material penetrates the micro pores before curing. PERMABOND® HL126 Threadlocker cures reliably and fast on most metallic surfaces. Features & Benefits: Prevents vibration loosening Controlled off-torque Full cure at room temperature Can be applied post assembly Ideal for sealing weld porosity Superior environmental resistance Environmentally friendly – 100% solids Information provided by Permabond.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.00 g/cc | 1.00 g/cc | Uncured |
| Viscosity | 10 - 30 cP @Temperature 25.0 °C |
10 - 30 cP @Temperature 77.0 °F |
Uncured |
| Storage Temperature | 5.00 - 25.0 °C | 41.0 - 77.0 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Adhesive Bond Strength | 10.0 - 20.0 MPa | 1450 - 2900 psi | steel collar and pin shear; ISO 10123 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | |
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 149 °C | 300 °F | |
| Minimum Service Temperature, Air | -53.9 °C | -65.0 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 11.0 kV/mm | 279 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 4.98 min @Temperature 23.0 °C |
0.0830 hour @Temperature 73.4 °F |
Brass, handling strength |
| 15.0 min @Temperature 23.0 °C |
0.250 hour @Temperature 73.4 °F |
M10 steel, handling strength | |
| 30.0 min @Temperature 23.0 °C |
0.500 hour @Temperature 73.4 °F |
Brass, working strength | |
| 60.0 min @Temperature 23.0 °C |
1.00 hour @Temperature 73.4 °F |
Aluminum, handling strength | |
| 60.0 - 180 min @Temperature 23.0 °C |
1.00 - 3.00 hour @Temperature 73.4 °F |
M10 steel, working strength | |
| 360 min @Temperature 23.0 °C |
6.00 hour @Temperature 73.4 °F |
Stainless steel, handling strength | |
| 1440 min @Temperature 23.0 °C |
24.0 hour @Temperature 73.4 °F |
Aluminum, working strength | |
| 1440 min @Temperature 23.0 °C |
24.0 hour @Temperature 73.4 °F |
M10 steel, full strength |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Green | Uncured |
| Maximum Gap Fill (mm) | 0.05 | |
| Maximum Thread Size | M10 | |
| Strength Retention | 50% at 150°C | Relative to 0°C |
| 80% at 100°C | Relative to 0°C | |
| 93% at 50°C | Relative to 0°C | |
| Torque Strength (N m) | 14 | M10 steel, break |
| 34 | M10 steel, prevail |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA - 2000 HF-4-2 High Impact Grade Acrylic Resin
- P & P Technology ECF-J Silver Aluminum Loaded Fluorosilicone
- Schott GM31684 Dental Glass
- Solvay Chemicals NOCOLOK® Zn Flux
- Shandong Rike Chemical RIKEâ„¢ RK-561 MBS Impact Modifier for PVC Opaque Product
- Covestro Baydur® 730 IBS Polyurethane Structural Foam RIM, Density 40 pcf, MDI-based 2-Component Liquid System
- Ensinger TECANYL™ MT XRO Autoclavable Polymer
- Abatron AboCast/AboCure 8110-1 Flexible Epoxy
- Aclo Accutech Polypropylene Copolymer CP0436C40L1 Calcium Reinforced
Copyright © lookpolymers.com All Rights Reserved