Cytec Thornel® VCL Carbon Cloth Laminate with Mil R-9299 Resin

Category Polymer , Thermoset , Carbon Fiber/Thermoset Composite , Epoxy , Epoxy/Carbon Fiber Composite , Filled/Reinforced Thermoset
Manufacturer Cytec
Trade Name Thornel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Cytec Thornel® VCL Carbon Cloth Laminate with Mil R-9299 Resin.pdf
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, Amoco Performance Products, Inc.Carbon and graphite cloths, consisting entirely of flexible filaments, are produced by pyrolysis of rayon cloth at high temperatures to yield products with a high degree of purity. The cloth flexibility results from the very small filament diameter. These are fair conductors of electricity. At room temperature the volume resistivity of graphite cloth is about 40 times that of "Nichrome" wire. Graphite cloth resistance decreases with temperature, reaching half of the room temperature value at 1315°C. Cloth carbon assay is 97%. Filament diameter is 8.9 µm.Thornel® products were sold by Amoco and are now owned by Cytec.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
Cloth 1.75 g/cc per He measurement
Mechanical Properties Metric English Comments
Hardness, Barcol 65
Tensile Strength, Ultimate 110 MPa
16000 psi
Tensile Modulus 15.0 GPa
2180 ksi
Flexural Yield Strength 170 MPa
24700 psi
Flexural Modulus 14.0 GPa
2030 ksi
Compressive Yield Strength 165 MPa
23900 psi
Compressive Modulus 11.0 GPa
1600 ksi
Thermal Properties Metric English Comments
CTE, linear 14.0 µm/m-°C

@Temperature 20.0 °C
7.78 µin/in-°F

@Temperature 68.0 °F
Specific Heat Capacity 1.20 J/g-°C
0.287 BTU/lb-°F
Thermal Conductivity 6.00 W/m-K
41.6 BTU-in/hr-ft²-°F