DuPont Performance Polymers Crastin® S600F40 NC010 PBT  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Crastin® S600F40 NC010 PBT  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Crastin® S600F40 NC010 is an unreinforced, lubricated, low viscosity polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.31 g/cc
0.0473 lb/in³
ISO 1183
Water Absorption 0.20 %

@Temperature 23.0 °C
 0.20 %

@Temperature 73.4 °F
 Equilibrium 50%RH; ISO 62, Similar to
0.40 %

@Temperature 23.0 °C
 0.40 %

@Temperature 73.4 °F
 Saturation, immersed; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.0225 cm/cm
0.0225 in/in
Annealed; ISO 294-4
0.0195 cm/cm

@Thickness 2.00 mm
 0.0195 in/in

@Thickness 0.0787 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.022 cm/cm
0.022 in/in
Annealed; ISO 294-4
0.018 cm/cm

@Thickness 2.00 mm
 0.018 in/in

@Thickness 0.0787 in
 ISO 294-4
Melt Flow 32.9 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 32.9 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 ISO 1133
Melt Index of Compound 32 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 32 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 cm3/10 min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 58.0 MPa

@Temperature 23.0 °C
 8410 psi

@Temperature 73.4 °F
 ISO 527
Elongation at Break 30 %

@Temperature 23.0 °C
 30 %

@Temperature 73.4 °F
 nominal; ISO 527
>= 50 %

@Temperature 23.0 °C
 >= 50 %

@Temperature 73.4 °F
 50mm/min; ISO 527
Elongation at Yield 6.0 %

@Temperature 23.0 °C
 6.0 %

@Temperature 73.4 °F
 ISO 527
Tensile Modulus 2.60 GPa

@Temperature 23.0 °C
 377 ksi

@Temperature 73.4 °F
 ISO 527
Flexural Strength 85.0 MPa

@Temperature 23.0 °C
 12300 psi

@Temperature 73.4 °F
 ISO 178
Flexural Modulus 2.40 GPa

@Temperature 23.0 °C
 348 ksi

@Temperature 73.4 °F
 ISO 178
Izod Impact, Notched (ISO) 4.00 kJ/m²

@Temperature 23.0 °C
 1.90 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/1A
Charpy Impact Unnotched NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 ISO 179/1eU
NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 0.400 J/cm²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
0.400 J/cm²

@Temperature 23.0 °C
 1.90 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Tensile Creep Modulus, 1 hour 2600 MPa

@Temperature 23.0 °C
 377000 psi

@Temperature 73.4 °F
 ISO 899
Tensile Creep Modulus, 1000 hours 1800 MPa

@Temperature 23.0 °C
 261000 psi

@Temperature 73.4 °F
 ISO 899
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 500 µm/m-°C

@Temperature 23.0 - 55.0 °C
 278 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1/-2
CTE, linear, Transverse to Flow 120 µm/m-°C

@Temperature 23.0 - 55.0 °C
 66.7 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1/-2
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 115 °C
239 °F
ISO 75-1/-2
180 °C
356 °F
Annealed; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 50.0 °C
122 °F
ISO 75-1/-2
60.0 °C
140 °F
Annealed; ISO 75-1/-2
Glass Transition Temp, Tg 55.0 °C
131 °F
10°C/min; ISO 11357-1/-2
UL RTI, Electrical 130 °C

@Thickness 0.750 mm
 266 °F

@Thickness 0.0295 in
 UL 746B
130 °C

@Thickness 1.50 mm
 266 °F

@Thickness 0.0591 in
 UL 746B
130 °C

@Thickness 6.00 mm
 266 °F

@Thickness 0.236 in
 UL 746B
130 °C

@Thickness 3.00 mm
 266 °F

@Thickness 0.118 in
 UL 746B
UL RTI, Mechanical with Impact 115 °C

@Thickness 1.50 mm
 239 °F

@Thickness 0.0591 in
 UL 746B
115 °C

@Thickness 0.750 mm
 239 °F

@Thickness 0.0295 in
 UL 746B
115 °C

@Thickness 3.00 mm
 239 °F

@Thickness 0.118 in
 UL 746B
115 °C

@Thickness 6.00 mm
 239 °F

@Thickness 0.236 in
 UL 746B
UL RTI, Mechanical without Impact 120 °C

@Thickness 0.750 mm
 248 °F

@Thickness 0.0295 in
 UL 746B
120 °C

@Thickness 3.00 mm
 248 °F

@Thickness 0.118 in
 UL 746B
120 °C

@Thickness 6.00 mm
 248 °F

@Thickness 0.236 in
 UL 746B
120 °C

@Thickness 1.50 mm
 248 °F

@Thickness 0.0591 in
 UL 746B
Flammability, UL94 HB

@Thickness 6.00 mm
 HB

@Thickness 0.236 in
 IEC 60695-11-10
HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 IEC 60695-11-10
HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
 IEC 60695-11-10
HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 UL94
HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
 UL94
HB

@Thickness 6.00 mm
 HB

@Thickness 0.236 in
 UL94
Oxygen Index 22 %
22 %
ISO 4589-1/-2
Glow Wire Test 750 °C

@Thickness 3.00 mm
 1380 °F

@Thickness 0.118 in
 IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm

@Temperature 23.0 °C
 >= 1.00e+15 ohm-cm

@Temperature 73.4 °F
 IEC 60093
Surface Resistance >= 1.00e+12 ohm

@Temperature 23.0 °C
 >= 1.00e+12 ohm

@Temperature 73.4 °F
 IEC 60093
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
 3.2

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
 IEC 60250
3.8

@Frequency 100 Hz,
Temperature 23.0 °C
 3.8

@Frequency 100 Hz,
Temperature 73.4 °F
 IEC 60250
3.8

@Frequency 50.0 Hz,
Temperature 23.0 °C
 3.8

@Frequency 50.0 Hz,
Temperature 73.4 °F
 IEC 60250
Dielectric Strength 26.0 kV/mm

@Thickness 2.00 mm
 660 kV/in

@Thickness 0.0787 in
 IEC 60243-1
26.0 kV/mm

@Thickness 1.00 mm,
Temperature 23.0 °C
 660 kV/in

@Thickness 0.0394 in,
Temperature 73.4 °F
 IEC 60243-1
Dissipation Factor 0.0020

@Frequency 100 Hz,
Temperature 23.0 °C
 0.0020

@Frequency 100 Hz,
Temperature 73.4 °F
 IEC 60250
0.0020

@Frequency 50.0 Hz,
Temperature 23.0 °C
 0.0020

@Frequency 50.0 Hz,
Temperature 73.4 °F
 IEC 60250
0.020

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
 0.020

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
 IEC 60250
Comparative Tracking Index 250 V

@Temperature 23.0 °C
 250 V

@Temperature 73.4 °F
 UL 746A
600 V

@Temperature 23.0 °C
 600 V

@Temperature 73.4 °F
 IEC 60112
Processing Properties Metric English Comments
Melt Temperature 250 °C
482 °F
Optimum
240 - 260 °C
464 - 500 °F
Mold Temperature 80.0 °C
176 °F
optimum
30.0 - 130 °C
86.0 - 266 °F
Drying Temperature 110 - 130 °C
230 - 266 °F
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Moisture Content <= 0.040 %
<= 0.040 %
Descriptive Properties Value Comments
Additive Lubricant
Appearance Natural Color