DuPont Performance Polymers Crastin® CE15315 BK010 PBT (Unverified Data**)

Category	Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Crastin® CE15315 BK010 PBT (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Crastin® CE15315 BK010 is a 15% glass reinforced flame retardant polybutylene terephthalate molding resin. It is recognized as UL94 V-0 at 0.71mm(0.028in).Information provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.493 g/cc	0.05394 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.0030 - 0.0050 cm/cm @Thickness 2.00 mm	0.0030 - 0.0050 in/in @Thickness 0.0787 in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.0050 - 0.0090 cm/cm @Thickness 2.00 mm	0.0050 - 0.0090 in/in @Thickness 0.0787 in	ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	91.0 MPa @Temperature 23.0 °C	13200 psi @Temperature 73.4 °F	ISO 527
Elongation at Break	2.8 % @Temperature 23.0 °C	2.8 % @Temperature 73.4 °F	ISO 527
Tensile Modulus	5.70 GPa @Temperature 23.0 °C	827 ksi @Temperature 73.4 °F	ISO 527
Charpy Impact Unnotched	2.15 J/cm² @Temperature -30.0 °C	10.2 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eU
	2.31 J/cm² @Temperature 23.0 °C	11.0 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	0.500 J/cm² @Temperature -30.0 °C	2.38 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	0.510 J/cm² @Temperature 23.0 °C	2.43 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	223 °C	433 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi)	195 °C	383 °F	ISO 75-1/-2
UL RTI, Electrical	130 °C @Thickness 0.710 mm	266 °F @Thickness 0.0280 in	UL 746B
	130 °C @Thickness 1.50 mm	266 °F @Thickness 0.0591 in	UL 746B
	130 °C @Thickness 3.00 mm	266 °F @Thickness 0.118 in	UL 746B
UL RTI, Mechanical with Impact	110 °C @Thickness 0.710 mm	230 °F @Thickness 0.0280 in	UL 746B
	110 °C @Thickness 1.50 mm	230 °F @Thickness 0.0591 in	UL 746B
	120 °C @Thickness 3.00 mm	248 °F @Thickness 0.118 in	UL 746B
UL RTI, Mechanical without Impact	130 °C @Thickness 0.710 mm	266 °F @Thickness 0.0280 in	UL 746B
	130 °C @Thickness 1.50 mm	266 °F @Thickness 0.0591 in	UL 746B
	130 °C @Thickness 3.00 mm	266 °F @Thickness 0.118 in	UL 746B
Flammability, UL94	V-0 @Thickness 0.710 mm	V-0 @Thickness 0.0280 in	UL94
	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in	UL94
	V-0 @Thickness 3.00 mm	V-0 @Thickness 0.118 in	UL94

Processing Properties	Metric	English	Comments
Melt Temperature	250 °C	482 °F	Optimum; Injection Molding
	240 - 260 °C	464 - 500 °F	Injection Molding
Mold Temperature	60.0 °C	140 °F	optimum; Injection Molding
	10.0 - 110 °C	50.0 - 230 °F	Injection Molding
Drying Temperature	100 - 140 °C	212 - 284 °F	Injection Molding
Dry Time	2.00 - 6.00 hour	2.00 - 6.00 hour	Injection Molding
Moisture Content	<= 0.040 %	<= 0.040 %	Injection Molding

Descriptive Properties	Value	Comments
Forms	Pellets
Generic	PBT
Material Status	Current
Part Marking Code	>PBT-GF15FR(17)<	ISO 11469
Processing Method	Injection Molding
Product Category	Extrusion Resins
	Glass Reinforced Resins
Resin Identification	PBT-GF15FR(17)	ISO 1043
RoHS Compliance	Contact Manufacturer