- Lehmann & Voss LUVOCOM® 80-7718 Polyacetal-copolymer, with PTFE, lubricant modified
Lehmann & Voss LUVOCOM® 80-7718 Polyacetal-copolymer, with PTFE, lubricant modified
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, PTFE Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 80-7718 Polyacetal-copolymer, with PTFE, lubricant modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Emergency running property, glide mating with low sliding friction.High dimensionally stable precision parts.Bearings, sleeves, high precision gear wheels, control disks, rollers, coil formers.No mass temperature above 215°C! Ventilation of machinery is recommended.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.018 - 0.030 cm/cm | 0.018 - 0.030 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 48.0 MPa | 6960 psi | |
| Elongation at Yield | 16 % | 16 % | |
| 20 % | 20 % | flexural | |
| Modulus of Elasticity | 2.30 GPa | 334 ksi | |
| Flexural Strength | 70.0 MPa | 10200 psi | |
| Flexural Modulus | 2.00 GPa | 290 ksi | |
| Charpy Impact Unnotched | 7.00 J/cm² | 33.3 ft-lb/in² | flatwise; ISO 179 1fU |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| 120 °C | 248 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | |
| Vicat Softening Point | 160 °C | 320 °F | DIN ISO 306 |
| Flammability, UL94 | HB | HB | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | |
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 °C | 392 °F | mass temp |
| Nozzle Temperature | 175 - 200 °C | 347 - 392 °F | |
| Zone 1 | 175 - 190 °C | 347 - 374 °F | |
| Zone 2 | 185 - 205 °C | 365 - 401 °F | |
| Zone 3 | 180 - 200 °C | 356 - 392 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 7200 - 28800 sec |
167 °F @Time 2.00 - 8.00 hour |
Dehumidifying dryer |
| 120 °C @Time 7200 - 14400 sec |
248 °F @Time 2.00 - 4.00 hour |
Air-Circulation Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Qualchem Danamid FGF-50 Polyamide 6, 50% Glass Fiber
- Overview of materials for Polycarbonate-Urethane
- Schott RG610 Long Pass Filter
- Shakespeare NX-806 Saltwater Nylon Copolymer Fishing Line, 80 lb
- Teknor Apex APEX® 3611-85 Polyvinyl Chloride, Flexible
- ExxonMobil Mobil 1 5W-50
- Total PPR 12222 Random Copolymer Polypropylene
- Biomer P209 PHB Biodegradable Polymer
- Momentive Performance Materials PolarTherm® PT620 Boron Nitride (BN) Powder
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR N339 Filler
Copyright © lookpolymers.com All Rights Reserved