- Lehmann & Voss LUVOCOM® 1105-7995 PEEK, with carbon fiber
Lehmann & Voss LUVOCOM® 1105-7995 PEEK, with carbon fiber
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1105-7995 PEEK, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High-strength and high-stiff parts; low coefficient of expansion.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts, non flammable.Electrically conductive, suitable for continuous discharging of statically generated electricity.Bearings, sleeves, control disks, gear wheels, pump impellers, gear parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.52 g/cc | 1.52 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.00050 - 0.0030 cm/cm | 0.00050 - 0.0030 in/in | |
| Melt Flow | 91.2 g/10 min @Load 10.0 kg, Temperature 380 °C |
91.2 g/10 min @Load 22.0 lb, Temperature 716 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 240 MPa | 34800 psi | |
| Elongation at Yield | 1.4 % | 1.4 % | |
| 1.9 % | 1.9 % | flexural | |
| Modulus of Elasticity | 24.0 GPa | 3480 ksi | |
| Flexural Strength | 445 MPa | 64500 psi | |
| Flexural Modulus | 20.0 GPa | 2900 ksi | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 250 °C | 482 °F | |
| 300 °C | 572 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 10000 ohm | <= 10000 ohm | |
| Insulation Resistance | <= 10000 ohm | <= 10000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
| 150 °C @Time 10800 - 21600 sec |
302 °F @Time 3.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | grey |
Users viewing this material also viewed the following:
- NIZHNEKAMSKNEFTEKHIM PE 4026Z (26460) Linear Low Density Polyethylene
- Advanced Elastomer Systems VistaFlex® 912-B Thermoplastic Rubber (discontinued **)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR N339 Filler
- Resin Technology Group KONA 870FT-FR Fire Retardant Epoxy Casting System
- Haynes 556® alloy, 30% cold reduction
- Solvay TECHNYL® A 50H1 PA66, Conditioned
- Samyang Trirex® 3030U Polycarbonate, UV Stabilized
- Goodfellow Alumina/Silica SiO2 20/Al2O3 80
- Zircar Zirconia ZOG Single Crystal Zirconia Grog Insulation
- Eagle Brass 240 Low Brass, 1/4 Hard
Copyright © lookpolymers.com All Rights Reserved