DSM EcoPaXX® Q-KGS6 PA410-GF30 FR
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | EcoPaXX® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM EcoPaXX® Q-KGS6 PA410-GF30 FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass Reinforced, Flame Retardant (Halogen free)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 1.10 % | 1.10 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0133 cm/cm | 0.0133 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 90.0 MPa | 13100 psi | cond; ISO 527-1/-2 |
| 135 MPa | 19600 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 2.5 % | 2.5 % | dry; ISO 527-1/-2 |
| 3.8 % | 3.8 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 7.70 GPa | 1120 ksi | cond; ISO 527-1/-2 |
| 10.0 GPa | 1450 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU |
| 4.50 J/cm² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU | |
| Charpy Impact, Notched | 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA |
| 0.750 J/cm² @Temperature 23.0 °C |
3.57 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C | 22.2 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 66.0 µm/m-°C | 36.7 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 250 °C | 482 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
dry; IEC 60695-11-10 |
| V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
dry; IEC 60695-11-10 | |
| Glow Wire Test | 775 °C @Thickness 0.800 mm |
1430 °F @Thickness 0.0315 in |
Glow Wire Ignition Temperature; IEC 60695-2-13 |
| 960 °C @Thickness 0.800 mm |
1760 °F @Thickness 0.0315 in |
Glow Wire Flammability Index; IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | cond; IEC 60093 |
| >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | dry; IEC 60093 | |
| Surface Resistance | 6.00e+13 ohm | 6.00e+13 ohm | cond; IEC 60093 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | cond; IEC 60243-1 |
| 40.0 kV/mm | 1020 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 600 V | 600 V | cond; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Calculated Bio Based Carbon Content (%) | 60 | ASTM 6866 |
Users viewing this material also viewed the following:
- PolyOne Versaflex™ CL2250 Thermoplastic Elastomer (TPE)
- Precision Polymer Engineering V90M Fluoroelastomer Compound
- Videolar 535 Crystal Polystyrene (GPPS)
- Total 50100.1 HDPE blow molding
- AdvanSource Biomaterials ChronoPrene™ 25A Thermoplastic Rubber Elastomer
- A. Schulman ComAlloy Comtuf® 602 Nylon 6/6, High Impact Modified
- Axiall 19853 Wire & Cable Flexible PVC
- Ineos Nova Zyntar® 779 High Performance Flame Retardant Polystyrene (discontinued **)
- SMAC CABLE® 2521S-30-08 Damping Material
Copyright © lookpolymers.com All Rights Reserved