Aremco Ceramabond™ 516 High Temperature Ceramic Adhesive/Paste, Zirconia Filled
| Category | Ceramic , Oxide , Zirconium Oxide |
| Manufacturer | Aremco |
| Trade Name | Ceramabond™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aremco Ceramabond™ 516 High Temperature Ceramic Adhesive/Paste, Zirconia Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Aremco's ceramic adhesives are easy to use, one- and two-component systems which air dry in 1-2 hrs and are ready for use following a 200 to 700 °F cure. These materials are mostly water-based and do not outgas after curing. They are also environmentally safe, non-flammable materials which contain no volatile organic compounds.General Features: Dielectric, Moisture Resistant Bonding: Ceramic to Ceramic, Ceramic to Metal, Metal to Metal Principal Use: Thermocouples
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.15 - 2.30 g/cc | 0.0777 - 0.0831 lb/in³ | |
| Viscosity | 40000 - 70000 cP | 40000 - 70000 cP | |
| Storage Temperature | 4.44 - 32.2 °C | 40.0 - 90.0 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Impact Test | 67.8 J | 50.0 ft-lb | Torque Strength; curing at 1000°F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 7.38 µm/m-°C | 4.10 µin/in-°F | |
| Maximum Service Temperature, Air | 1760 °C | 3200 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10000 ohm-cm @Temperature 538 °C |
10000 ohm-cm @Temperature 1000 °F |
|
| 1.00e+8 ohm-cm @Temperature 23.0 °C |
1.00e+8 ohm-cm @Temperature 73.4 °F |
||
| Dielectric Strength | 7.40 kV/mm | 188 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 420 - 600 min | 7.00 - 10.0 hour | 1-4 hrs Air Set; 2 hrs at 200°F; 2 hrs at 500°F; 2 hrs at 700°F |
| Shelf Life | 6.00 Month @Temperature 4.44 - 32.2 °C |
6.00 Month @Temperature 40.0 - 90.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Acid Resistance | Good | after curing at 700°F for 2 hours |
| Alkali Resistance | Excellent | after curing at 700°F for 2 hours |
| Color | Tan | |
| Moisture Resistance | Good | after curing at 700°F for 2 hours |
Users viewing this material also viewed the following:
- Kennametal Stellite Deloro® 711 PM cast
- H.C. Starck Grade A Silicon Hexaboride, SiB6
- KaMin Polyfil® DL Kaolin Clay - Delaminated
- SABIC Innovative Plastics LNP LUBRICOMP UFL36S PPA
- Solvay Specialty Polymers FOMBLIN® Y25 PFPE Lubricant
- Techmer ES HiFill® PEEK CF30 HF 30% Carbon Filled
- Stir SpA IN 3080 (PVC)
- Polyram PlusTek PB841 Nylon 6 for Injection Molding, Impact Modified
- Fainplast Compounds GA 77/1 Flexible PVC, Flame Retardant Sheathing
- A. Schulman ComAlloy Comtuf® 613 Nylon 6, Glass Reinforced, Impact Modified
Copyright © lookpolymers.com All Rights Reserved