DSM Akulon® K224-G6-FC NA99001 PA6-GF30

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer DSM Engineering Plastics
Trade Name Akulon®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DSM Akulon® K224-G6-FC NA99001 PA6-GF30.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% Glass Reinforced, Food Contact Grade
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
dry; ISO1183
Water Absorption 6.3 %
6.3 %
Sim. To ISO 62
Moisture Absorption 1.90 %
1.90 %
Sim. To ISO 62
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
0.0090 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 110 MPa
16000 psi
cond; ISO 527-1/-2
180 MPa
26100 psi
dry; ISO 527-1/-2
Elongation at Break 3.5 %
3.5 %
dry; ISO 527-1/-2
7.0 %
7.0 %
cond; ISO 527-1/-2
Tensile Modulus 6.00 GPa
870 ksi
cond; ISO 527-1/-2
9.50 GPa
1380 ksi
dry; ISO 527-1/-2
Flexural Strength 235 MPa
34100 psi
dry; ISO 178
Flexural Modulus 8.60 GPa
1250 ksi
dry; ISO 178
Charpy Impact Unnotched 7.50 J/cm²

@Temperature -30.0 °C
35.7 ft-lb/in²

@Temperature -22.0 °F
cond; ISO 179/1eU
7.50 J/cm²

@Temperature -30.0 °C
35.7 ft-lb/in²

@Temperature -22.0 °F
dry; ISO 179/1eU
9.00 J/cm²

@Temperature 23.0 °C
42.8 ft-lb/in²

@Temperature 73.4 °F
dry; ISO 179/1eU
11.0 J/cm²

@Temperature 23.0 °C
52.3 ft-lb/in²

@Temperature 73.4 °F
cond; ISO 179/1eU
Charpy Impact, Notched 1.10 J/cm²

@Temperature -30.0 °C
5.23 ft-lb/in²

@Temperature -22.0 °F
dry; ISO 179/1eA
1.10 J/cm²

@Temperature -30.0 °C
5.23 ft-lb/in²

@Temperature -22.0 °F
cond; ISO 179/1eA
1.20 J/cm²

@Temperature 23.0 °C
5.71 ft-lb/in²

@Temperature 73.4 °F
dry; ISO 179/1eA
2.50 J/cm²

@Temperature 23.0 °C
11.9 ft-lb/in²

@Temperature 73.4 °F
cond; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 µm/m-°C
11.1 µin/in-°F
dry; ISO 11359-1/-2
CTE, linear, Transverse to Flow 70.0 µm/m-°C
38.9 µin/in-°F
dry; ISO 11359-1/-2
Melting Point 220 °C
428 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
dry; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
dry; ISO 75-1/-2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
cond; IEC 60093
1.00e+15 ohm-cm
1.00e+15 ohm-cm
dry; IEC 60093
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
cond; IEC 60093
Dielectric Constant 3.3

@Frequency 1.00e+6 Hz
3.3

@Frequency 1.00e+6 Hz
dry; IEC 60250
3.5

@Frequency 100 Hz
3.5

@Frequency 100 Hz
dry; IEC 60250
5.0

@Frequency 1.00e+6 Hz
5.0

@Frequency 1.00e+6 Hz
cond; IEC 60250
20

@Frequency 100 Hz
20

@Frequency 100 Hz
cond; IEC 60250
Dielectric Strength 25.0 kV/mm
635 kV/in
cond; IEC 60243-1
30.0 kV/mm
762 kV/in
dry; IEC 60243-1
Dissipation Factor 0.0050

@Frequency 100 Hz
0.0050

@Frequency 100 Hz
dry; IEC 60250
0.015

@Frequency 1.00e+6 Hz
0.015

@Frequency 1.00e+6 Hz
dry; IEC 60250
0.12

@Frequency 1.00e+6 Hz
0.12

@Frequency 1.00e+6 Hz
cond; IEC 60250
0.30

@Frequency 100 Hz
0.30

@Frequency 100 Hz
cond; IEC 60250
Comparative Tracking Index 600 V
600 V
cond; IEC 60112