DSM Akulon® K224-G6-FC 99.99.99 PA6-GF30
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Akulon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Akulon® K224-G6-FC 99.99.99 PA6-GF30.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass Reinforced, Food Contact Grade
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | dry; ISO 1183 |
| Water Absorption | 6.3 % | 6.3 % | Sim. To ISO 62 |
| Moisture Absorption | 1.90 % | 1.90 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | cond; ISO 527-1/-2 |
| 180 MPa | 26100 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 3.5 % | 3.5 % | dry; ISO 527-1/-2 |
| 7.0 % | 7.0 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 6.00 GPa | 870 ksi | cond; ISO 527-1/-2 |
| 9.50 GPa | 1380 ksi | dry; ISO 527-1/-2 | |
| Flexural Strength | 235 MPa | 34100 psi | dry; ISO 178 |
| Flexural Modulus | 8.60 GPa | 1250 ksi | dry; ISO 178 |
| Charpy Impact Unnotched | 7.50 J/cm² @Temperature -30.0 °C |
35.7 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eU |
| 7.50 J/cm² @Temperature -30.0 °C |
35.7 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eU | |
| 9.00 J/cm² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU | |
| 11.0 J/cm² @Temperature 23.0 °C |
52.3 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU | |
| Charpy Impact, Notched | 1.10 J/cm² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eA |
| 1.10 J/cm² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eA | |
| 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA | |
| 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | dry; ISO 75-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | cond; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | dry; IEC 60093 | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | cond; IEC 60093 |
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz |
3.3 @Frequency 1.00e+6 Hz |
dry; IEC 60250 |
| 3.5 @Frequency 100 Hz |
3.5 @Frequency 100 Hz |
dry; IEC 60250 | |
| 5.0 @Frequency 1.00e+6 Hz |
5.0 @Frequency 1.00e+6 Hz |
cond; IEC 60250 | |
| 20 @Frequency 100 Hz |
20 @Frequency 100 Hz |
cond; IEC 60250 | |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | cond; IEC 60243-1 |
| 30.0 kV/mm | 762 kV/in | dry; IEC 60243-1 | |
| Dissipation Factor | 0.0050 @Frequency 100 Hz |
0.0050 @Frequency 100 Hz |
dry; IEC 60250 |
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
dry; IEC 60250 | |
| 0.12 @Frequency 1.00e+6 Hz |
0.12 @Frequency 1.00e+6 Hz |
cond; IEC 60250 | |
| 0.30 @Frequency 100 Hz |
0.30 @Frequency 100 Hz |
cond; IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | cond; IEC 60112 |
Users viewing this material also viewed the following:
- Nilit FRIANYL B63 S Nylon 6 for injection molding
- Parker Chomerics METALASTIC® Gasketing Wire Mesh EMI Gasket Selection Guide
- Plenco 2424 Phenolic, Granular, Injection Molded (discontinued **)
- Lehmann & Voss LUVOCOM® 1850-7942/RD PBT, with PTFE, lubricant modified
- SABIC Innovative Plastics LNP STAT-LOY NX03583 PC+ABS
- American Elements Nickel Oxide Nanopowder
- Crucible Steel 422 (JIS SUH616) Martensitic Steel
- ExxonMobil LLDPE LL 3003.32 Linear Low Density Polyethylene Resin
- ArcelorMittal 260 BH Bake hardening steel, Cold rolled
- 3M 7620/7890 White Vinyl Label Material
Copyright © lookpolymers.com All Rights Reserved