- Lehmann & Voss LUVOCOM® 50-7154/V0 Polycarbonate, with carbon fiber, low-warpage
Lehmann & Voss LUVOCOM® 50-7154/V0 Polycarbonate, with carbon fiber, low-warpage
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Carbon Fiber Reinforced |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 50-7154/V0 Polycarbonate, with carbon fiber, low-warpage.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Strong, stiff parts.Reduced moment of inertia compared with metal parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.High dimensionally stable precision parts with low warpage and narrow tolerance range.Body and duty parts in office equipment, gear wheels, grippers.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ISO 1183 |
| Water Absorption | <= 0.20 % | <= 0.20 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in | |
| Melt Flow | 13.1 g/10 min @Load 1.20 kg, Temperature 300 °C |
13.1 g/10 min @Load 2.65 lb, Temperature 572 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 105 MPa | 15200 psi | |
| Elongation at Yield | 2.8 % | 2.8 % | |
| 3.2 % | 3.2 % | flexural | |
| Modulus of Elasticity | 9.00 GPa | 1310 ksi | |
| Flexural Strength | 145 MPa | 21000 psi | |
| Flexural Modulus | 7.00 GPa | 1020 ksi | |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 130 °C | 266 °F | |
| 150 °C | 302 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | |
| Vicat Softening Point | 160 °C | 320 °F | DIN ISO 306 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 10000 ohm | <= 10000 ohm | |
| Insulation Resistance | <= 10000 ohm | <= 10000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 295 °C | 563 °F | mass temp |
| Nozzle Temperature | 290 - 310 °C | 554 - 590 °F | |
| Zone 1 | 280 - 300 °C | 536 - 572 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 300 - 320 °C | 572 - 608 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 120 °C @Time 14400 - 21600 sec |
248 °F @Time 4.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Rogers Corporation Poron® 4701-30-15 Cellular Urethane Foam
- Polimeri Europa Intol® 1723 Emulsion Styrene-Butadiene Rubber
- Wellman Wellamid® GF20-60 XE-N 20% Glass Fiber Reinforced Nylon 6, Lubricated & Heat Stabilized
- A. Schulman SCHULAMID® 66 GF33 33% Glass Fiber Reinforced Nylon 66
- EMS-Grivory Grivory® BG-35 PA6-GF35
- ChevronTexaco GST® ISO 68 Oil
- Alliance BCNF-30 Bonded (Composite) Magnetic Material
- ACC QM 118 QSI Quantum Silicones 18 Durometer Condensation Cured Moldmaking Material
- BASF Elastollan® 695A15N Polyester Type Polyurethane Elastomer
- Solvay RHODASURF® TR/15-40 Surfactant
Copyright © lookpolymers.com All Rights Reserved