Clariant Renol PA2SP0003 Nylon 6, High Gloss
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol PA2SP0003 Nylon 6, High Gloss.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.018 cm/cm | 0.018 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 44.8 MPa | 6500 psi | ASTM D638 |
| Flexural Modulus | 1.17 GPa | 170 ksi | ASTM D790 |
| Izod Impact, Notched | 8.01 J/cm @Temperature 22.8 °C |
15.0 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 227 - 254 °C | 440 - 490 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Dry Time | 2 - 4 hour @Temperature 71.1 °C |
2 - 4 hour @Temperature 160 °F |
to ensure moisture content is less than 0.2% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- Polykemi AB POLYelast TPE S902A Thermoplastic Elastomer, SBS-based
- DuPont™ Sclairfilm® LX-3 LLDPE Film, Laminating, 50.8 µm Thickness (discontinued **)
- Hardwire 12x-23-12 High Density Composite
- Plastics Group Polifil® RMC-20V 20% Calcium Carbonate-Reinforced Polypropylene, High Impact, UV Stabilized
- ExxonMobil Mobil Delvac 15W-40 1300 Super
- Chesterton 278 Super Solv
- Cytec Conathane® CC-1194 (Conap) Polyurethane Dielectric Conformal Coating
- Compuestos Dominicanos Polycom CE-553165 PVC Compound
- Lubrizol Estane® 2102-55D Thermoplastic Polyurethane Elastomer
Copyright © lookpolymers.com All Rights Reserved