Material Notes:

AK Steel 17-4 PH® provides an outstanding combination of high strength, good corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C), and good toughness in both base metal and welds. Short-time, low-temperature heat treatments minimize distortion and scaling. This alloy is widely used in the aerospace, chemical, petrochemical, food processing, paper and general metalworking industries. The material supplied from the mill is in Condition A. After fabrication eight standard heat treatments have been developed to provide a wide range of properties.Information provided by AK Steel

Physical Properties	Metric	English	Comments
Density	7.80 g/cc	0.282 lb/in³	Typical

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell C	33	33
Tensile Strength, Ultimate	1034 MPa	150000 psi
Tensile Strength, Yield	896 MPa @Strain 0.200 %	130000 psi @Strain 0.200 %
Elongation at Break	12 %	12 %	in 2 inches

Component Elements Properties	Metric	English	Comments
Carbon, C	<= 0.070 %	<= 0.070 %
Chromium, Cr	15 - 17.5 %	15 - 17.5 %
Copper, Cu	3.0 - 5.0 %	3.0 - 5.0 %
Iron, Fe	69.91 - 78.85 %	69.91 - 78.85 %	As Remainder
Manganese, Mn	<= 1.0 %	<= 1.0 %
Nb + Ta	0.15 - 0.45 %	0.15 - 0.45 %
Nickel, Ni	3.0 - 5.0 %	3.0 - 5.0 %
Phosphorous, P	<= 0.040 %	<= 0.040 %
Silicon, Si	<= 1.0 %	<= 1.0 %
Sulfur, S	<= 0.030 %	<= 0.030 %