Techmer ES Elastoblend® PA6 IM 7040 MB
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Heat Stabilized , Nylon 6, Impact Grade , Nylon 6, Nucleated |
| Manufacturer | Techmer ES |
| Trade Name | Elastoblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Elastoblend® PA6 IM 7040 MB.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier, Nucleating Agent and LubricantFeatures: Heat Stabilized, Impact Modified, Nucleated and LubricatedInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Water Absorption | 1.5 % @Time 86400 sec |
1.5 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0013 cm/cm @Thickness 3.17 mm |
0.0013 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 109 | 109 | ASTM D785 |
| Tensile Strength, Yield | 55.2 MPa | 8000 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Flexural Strength | 9.65 MPa | 1400 psi | ASTM D790 |
| Flexural Modulus | 1.72 GPa | 250 ksi | ASTM D790 |
| Izod Impact, Notched | 3.20 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
6.00 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| 4.54 J/cm @Thickness 3.17 mm, Temperature -20.0 °C |
8.50 ft-lb/in @Thickness 0.125 in, Temperature -4.00 °F |
ASTM D256 | |
| 6.41 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
12.0 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 95.4 µm/m-°C | 53.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 171 °C | 340 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 18.1 kV/mm | 460 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3991 TPE, PP Overmold or Standalone use
- Oxford Polymers PEI 10GF-Natural PEI, 10% Glass Fiber Reinforced
- MV Labs TM1000 Tm2(SO4)3·8H2O Thulium sulfate octahydrate
- LATI LARPEEK 10 G/30 30% Glass Reinforced Polyetheretherketone (PEEK) (Unverified Data**)
- Overview of materials for Nylon 66, Unreinforced
- Minelco UltraCarb LH15 Hydrated Magnesium Calcium Carbonate
- Diamond Polymers ASA TWP 121
- Dow AFFINITY™ SM 8400 Polyolefin Elastomer
- Arkema Group Nakan® FSS 703 R PVC, Soft Injection Molding Grade
Copyright © lookpolymers.com All Rights Reserved