Clariant PA213M40 Nylon 6, 40% Mineral Reinforced, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Mineral Filled , Nylon 6, Heat Stabilized
Manufacturer Clariant
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Clariant PA213M40 Nylon 6, 40% Mineral Reinforced, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by Clariant Masterbatches
Physical Properties Metric English Comments
Specific Gravity 1.49 g/cc
1.49 g/cc
ASTM D792
Filler Content 40 %
40 %
ASTM D2584
Linear Mold Shrinkage, Flow 0.0060 cm/cm
0.0060 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 75.8 MPa
11000 psi
ASTM D638
Elongation at Yield 3.0 %
3.0 %
ASTM D638
Flexural Yield Strength 124 MPa
18000 psi
ASTM D790
Flexural Modulus 5.52 GPa
800 ksi
ASTM D790
Izod Impact, Notched 0.481 J/cm

@Temperature 22.8 °C
 0.900 ft-lb/in

@Temperature 73.0 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 249 - 266 °C
480 - 510 °F
Middle Barrel Temperature 249 - 266 °C
480 - 510 °F
Front Barrel Temperature 254 - 271 °C
490 - 520 °F
Nozzle Temperature 254 - 274 °C
490 - 525 °F
Melt Temperature 254 - 271 °C
490 - 520 °F
Mold Temperature 79.4 - 121 °C
175 - 250 °F
Dry Time 2 - 4 hour

@Temperature 79.4 °C
 2 - 4 hour

@Temperature 175 °F
 to ensure moisture content is less than 0.2%
Injection Pressure 4.96 - 8.27 MPa
720 - 1200 psi
Secondary
8.27 - 13.8 MPa
1200 - 2000 psi
Initial
Back Pressure 0.345 MPa
50.0 psi
Shot Size 30 - 80 %
30 - 80 %
Screw Speed 20 - 100 rpm
20 - 100 rpm