- Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
- Chi Mei Polylac® PA-765 ABS - Flame Retardant
Chi Mei Polylac® PA-765 ABS - Flame Retardant
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Polylac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Polylac® PA-765 ABS - Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
F.R. High Flow
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 5.2 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.2 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| 60 g/10 min @Load 10.0 kg, Temperature 220 °C |
60 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO-1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Ball Indentation Hardness | 79.0 MPa | 11500 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 34.0 MPa | 4930 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 39.0 MPa | 5660 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 10 % | 10 % | 50 mm/min; ISO 527 |
| Flexural Strength | 55.0 MPa | 7980 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.80 GPa | 261 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 1.83 J/cm @Thickness 6.35 mm |
3.43 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 2.22 J/cm @Thickness 3.17 mm |
4.16 ft-lb/in @Thickness 0.125 in |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180/1C |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179 |
| Impact | 12.0 | 12.0 | Impact Flexural Test Notched (KJ/m²) |
| NB | NB | Impact Flexural Test Unnotched (KJ/m²) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | unannealed; ISO 75 |
| 90.0 °C | 194 °F | annealed; ISO 75 | |
| Vicat Softening Point | 78.0 °C @Load 5.00 kg |
172 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 80.0 °C @Load 5.00 kg |
176 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 90.0 °C @Load 1.00 kg |
194 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| 90.0 °C @Load 1.00 kg |
194 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| Flammability, UL94 | V-0 @Thickness 1.59 mm |
V-0 @Thickness 0.0625 in |
UL 94 |
| 5VA @Thickness 2.54 mm |
5VA @Thickness 0.100 in |
UL 94 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 177 °C | 350 °F | |
| Middle Barrel Temperature | 204 °C | 400 °F | |
| Front Barrel Temperature | 216 °C | 420 °F | |
| Melt Temperature | 232 - 249 °C | 450 - 480 °F | Nozzle temp not greater than stock |
| Mold Temperature | 54.4 - 71.1 °C | 130 - 160 °F | |
| Drying Temperature | 87.8 - 93.3 °C | 190 - 200 °F | |
| Dry Time | 2 - 24.0 hour | 2 - 24.0 hour | |
| Injection Pressure | 55.2 - 82.7 MPa | 8000 - 12000 psi | |
| Back Pressure | 0.689 MPa | 100 psi | |
| Screw Speed | 50 - 60 rpm | 50 - 60 rpm |
Users viewing this material also viewed the following:
- Osprey Metals 304L/MA Master Alloy Stainless Steel Powder (Grade 90% - 22)
- Polykemi AB POLYfill PPH T2040 Polypropylene Homopolymer, Mineral Reinforced
- LyondellBasell Pro-faxâ„¢ SR257M Polypropylene Copolymer
- Ineos K38-20-188 HDPE
- Hippe PBT Polybutylene Terephthalate
- ArcelorMittal Dual Phase 600 Very high strength steel, Cold Rolled Steel
- Colorite Polymers 7066 Non-Phthalate 66 Series Vinyl Compound
- Kolon Kopa® KN153G15 Nylon 6 Resin
- Henkel Hysol MA 562SFR Core Splice Adhesive
Copyright © lookpolymers.com All Rights Reserved