Asahi Kasei Thermylene® P6-10FG-0570 10% Glass Fiber Reinforced, Flame Retardant
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Glass Fiber Filler |
| Manufacturer | Asahi Kasei |
| Trade Name | Thermylene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Thermylene® P6-10FG-0570 10% Glass Fiber Reinforced, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asahi Thermofil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | ASTM D955 |
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 94 | 94 | ASTM D785 |
| Tensile Strength, Yield | 50.3 MPa | 7300 psi | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 68.9 MPa | 10000 psi | ASTM D790 |
| Flexural Modulus | 2.90 GPa | 420 ksi | ASTM D790 |
| Izod Impact, Notched | 0.934 J/cm | 1.75 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.74 J/cm | 7.00 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 146 °C | 295 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | 0.0279 in thickness |
Users viewing this material also viewed the following:
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 40 PHR N990 (MT) Filler
- Honeywell ACLAR® 22C (5.00 mil) Copolymer Film (discontinued **)
- Kinlead PG12 Bag Grade BOPP Plain Film (thickness: 40 µm)
- Intercontinental Polymers 1128 Bicomponent PBT/PET Fiber Type - 1.8 Denier X 3 Inches
- Momentive Performance Materials TSE 221-4U Heat Cured Rubber
- SABIC Innovative Plastics ULTEM CRS5011R PEI (Europe-Africa-Middle East)
- Zircar Zirconia ZYBF-3 Zirconia Bulk Fiber Insulation
- EMS-Grivory Grivory® 2D 25 W 20 X black PA612-I
- Arlon R35948R015 0.0155" (0.394 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- LyondellBasell Hifax™ CA186 Thermoplastic Olefin Resin