- Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
- Chi Mei Polylac® PA-763 ABS - Flame Retardant
Chi Mei Polylac® PA-763 ABS - Flame Retardant
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Polylac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Polylac® PA-763 ABS - Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
F.R. High Heat Weather Resistant
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Melt Flow | 30 g/10 min @Load 10.0 kg, Temperature 220 °C |
30 g/10 min @Load 22.0 lb, Temperature 428 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 80.0 MPa | 11600 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 32.0 MPa | 4640 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 15 % | 15 % | 50 mm/min; ISO 527 |
| Flexural Strength | 59.0 MPa | 8560 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 20.0 GPa | 2900 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180/1C |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179 |
| Impact | 13.0 | 13.0 | Impact Flexural Test Notched (KJ/m²) |
| NB | NB | Impact Flexural Test Unnotched (KJ/m²) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | unannealed; ISO 75 |
| 96.0 °C | 205 °F | annealed; ISO 75 | |
| Vicat Softening Point | 96.0 °C @Load 5.00 kg |
205 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 97.0 °C @Load 5.00 kg |
207 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 103 °C @Load 1.00 kg |
217 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| 104 °C @Load 1.00 kg |
219 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | V-0 @Thickness 1.59 mm |
V-0 @Thickness 0.0625 in |
UL 94 |
| 5VB @Thickness 2.54 mm |
5VB @Thickness 0.100 in |
UL 94 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL1192T PC Copolymer (Asia Pacific)
- MetalTek MTEK CX-2MW Cast UNS N26022 Severe Corrosion and Heat Resistant Alloy
- SABIC Innovative Plastics Valox® IQ325HP PBT (Asia Pacific)
- A. Schulman POLYBATCH™ White LL8855 GP Concentrate Based In LLDPE
- A. Schulman SCHULAMID® 66 GF33H 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66
- DSM Novamid® ST120 NAT PA6-I
- Asahi Kasei Thermylene® P6-20FG-2153R 20% Glass Fiber Reinforced, Heat Stabilized
- SABIC Innovative Plastics LNP LUBRICOMP DFP32 PC
- Lubrizol ESTANE® 58202 Ether Based Thermoplastic Polyurethane (European Grade)
- Advanced Elastomer Systems Trefsin® 3101-65 W305 Thermoplastic Rubber (discontinued **)
Copyright © lookpolymers.com All Rights Reserved