Americas Styrenics STYRON A-TECH® 1400AS High Impact Polystyrene
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Americas Styrenics LLC |
| Trade Name | STYRON A-TECH® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Americas Styrenics STYRON A-TECH® 1400AS High Impact Polystyrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product CharacteristicsHigh FlowGood ImpactFood Contact CompliantTypical ApplicationsTelevision housingsPrinter HousingsConsumer goodsInformation provided by AmericasStyrenics LLC.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 9.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
9.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 103 | 103 | ASTM D785 |
| Tensile Strength at Break | 21.4 MPa | 3100 psi | ASTM D638 |
| Tensile Strength | 22.1 MPa | 3200 psi | ASTM D638 |
| Elongation at Break | 70 % | 70 % | ASTM D638 |
| Tensile Modulus | 1.72 GPa | 250 ksi | ASTM D638 |
| Flexural Strength | 31.0 MPa | 4500 psi | ASTM D790 |
| Flexural Modulus | 1.72 GPa | 250 ksi | ASTM D790 |
| Izod Impact, Notched | 0.854 J/cm | 1.60 ft-lb/in | compression molded; ASTM D256 |
| 1.07 J/cm | 2.00 ft-lb/in | injection molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.8 °C | 172 °F | ASTM D648 |
| Vicat Softening Point | 100 °C | 212 °F | ASTM D1525 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66/6 GF 20 PA66/6, 20% glass fibre
- SABIC Innovative Plastics Lexan® LSHF PC (Asia Pacific)
- Honeywell ACLAR® SupRx 900 CTFE Homopolymer, Barrier Film
- ExxonMobil Enmist EP 460
- Lubrizol ESTANE® GP92AB Ester Based Thermoplastic Polyurethane (European Grade)
- Tipco Tipcolene® SEB 300 M - 30% Chemically Coupled Glass Fibers & Mineral Polypropylene Homopolymer
- Ecomass® 1050CO94 Copper Filled Polyamide
- Elastocon TPE Technologies Elastocon® 8068L Thermoplastic Elastomer
- Bapolene® 108A Low Density Polyethylene Film Extrusion Resin
- DuPont Performance Polymers Neoprene AC SOFT Polychloroprene Rubber (discontinued **)
Copyright © lookpolymers.com All Rights Reserved