Chi Mei Kibisan® PN-106 L150 SAN
| Category | Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Molded |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Kibisan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Kibisan® PN-106 L150 SAN.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High Clarity
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 |
| Melt Flow | 32 g/10 min @Load 10.0 kg, Temperature 220 °C |
32 g/10 min @Load 22.0 lb, Temperature 428 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 155 MPa | 22500 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 54.0 MPa | 7830 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| Flexural Strength | 92.0 MPa | 13300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.00 GPa | 435 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ISO 180/1C |
| Charpy Impact Unnotched | 1.80 J/cm² | 8.57 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | ISO 179 |
| Impact | 3.00 | 3.00 | Impact Flexural Test Notched (KJ/m²) |
| 18.0 | 18.0 | Impact Flexural Test Unnotched (KJ/m²) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | unannealed; ISO 75 |
| 97.0 °C | 207 °F | annealed; ISO 75 | |
| Vicat Softening Point | 101 °C @Load 5.00 kg |
214 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 103 °C @Load 5.00 kg |
217 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 105 °C @Load 1.00 kg |
221 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| 108 °C @Load 1.00 kg |
226 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
UL 94 |
Users viewing this material also viewed the following:
- Overview of materials for Nylon 612, Impact Modified
- H.C. Starck Amperit® 740.3 Aluminum Oxide (Al2O3)
- SABIC Innovative Plastics Valox® 310SE0 PBT (Europe-Africa-Middle East)
- Clariant PCSP0014 GREY Polycarbonate, Stainless Steel Fiber, EMI
- Alliance Polymers Viprene™ P55D-22U-NAT Thermoplastic Vulcanizate Elastomer
- Ascend Performance Materials Vydyne® 21SPG1 Nylon 66, DAM
- Adell BW-17 Nylon 6, 35% Glass Reinforced; Superior Finish
- Kennametal Stellite Deloro® N-6 PM cast
Copyright © lookpolymers.com All Rights Reserved