Polymer Property : Flexural Strength = 92.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	92.0 MPa	13300 psi	ASTM D790
Solvay Specialty Polymers Amodel® AT-5001 Polyphthalamide (PPA) Resin, Dry as Molded (discontinued **) AMODEL AT-5001 polyphthalamide resin is a neat ductile material that offers superior retention of properties after humid thermal aging, high impact at low temperature, and better mechanical properti..
Flexural Strength	<= 92.0 MPa	<= 13300 psi	ISO 178
Polykemi AB POLYshine PBT D201 T20 PBT, Reinforced Information provided by Polykemi AB
Flexural Strength	92.0 MPa	13300 psi	ASTM D790
Rostone Rosite® 4950BS SMC Thermoset Polyester, 10% Glass Reinforced (discontinued **) Key Features: Low Shrink; Tight DimensionsRemarkable physical and electrical strength combined with excellent dimensional stability. Information provided by Oneida-Rostone Group.
Flexural Strength	92.0 MPa	13300 psi	2mm/min; ASTM D790
Kingfa JH710 G10D Flame Retardant & 10% Glass Fiber Reinforced PC Features:Environmental friendly flame retardantUL V-0 @ 1.6mmHigh mechanical strengthGood size stability, good surfaceSuitable for exact moldingApplications:Exact mechanism partsElectrical and elect..
Flexural Strength	92.0 MPa	13300 psi	ASTM D790
Kolon KOCETALÂ® DS500 Acid Resistant Acetal Resin Improved acid resistance. Applications: Products for improved chemical resistance. Information provided by API-Kolon.
Flexural Strength	92.0 MPa	13300 psi	ASTM D790
Kolon KOCETALÂ® LF701 Wear Modified Acetal Resin Special polymer added, improved wear property. Applications: Products for low noise and precision gear. Information provided by API-Kolon.
Flexural Strength	92.0 MPa	13300 psi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP KZL16 Acetal Copolymer LNP LUBRICOMP* KZL16 is a compound based on Acetal Copolymer resin containing Glass Fiber, Milled Glass, PTFE. Added features of this material include: Internally Lubricated.
Flexural Strength	92.0 MPa	13300 psi	2 mm/min; ISO 178
SABIC Innovative Plastics XYLEX X7509HP PC+POLYESTER PC+Polyester alloy. Houseware applications. USA/Europe Food contact. this grade will no longer be supported with biocompatibility information and should not be used for medical applications which r..
Flexural Strength	92.0 MPa	13300 psi	2 mm/min; ISO 178
SABIC Innovative Plastics XYLEX X7509HP PC+POLYESTER (Europe-Africa-Middle East) PC+Polyester alloy. Houseware applications. USA/Europe Food contact. this grade will no longer be supported with biocompatibility information and should not be used for medical applications which r..
Flexural Strength	92.0 MPa	13300 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP AX06437 ABS LNP* THERMOCOMP* AX06437 is a compound based on ABS resin containing Proprietary Filler(s). Added feature of this grade is: Platable.
Flexural Strength	92.0 MPa	13300 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP AX08306 ABS LNP* THERMOCOMP* AX08306 is a compound based on ABS resin containing Proprietary Filler(s). Added feature of this grade is: Platable.
Flexural Strength	92.0 MPa	13300 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP AX08306 ABS (Asia Pacific) LNP* Thermocomp* AX08306 is a compound based on Acrylonitrile Butadiene Styrene resin containing Mineral.
Flexural Strength	92.0 MPa	13300 psi	2mm/min; ISO 178
Teijin PanliteÂ® L-1225Y Standard (mold release/ice color grade) Polycarbonate Resin Injection molding and small-sized injection-blow molding grade that require slightly high fluidity. It has an improved mold release property and is bluish-tinted to exhibit clear color.Applications:..
Flexural Strength	92.0 MPa	13300 psi	2mm/min; ISO 178
Teijin PanliteÂ® LN-2250Y Flame Resistant, Translucent Polycarbonate Resin Flame retardant and mold release grade with normal fluidity, while maintaining intrinsic transparency of polycarbonate resin. It is suitable for injection molding applications.Applications:Electric,..
Flexural Strength	92.0 MPa	13300 psi	2mm/min; ISO 178
Teijin PanliteÂ® LV-2225Y Standard (mold release/ice color grade) Polycarbonate Resin Flame retardant and mold release grade, while maintaining intrinsic transparency of polycarbonate resin. It is suitable for injection molding applications, required to be slightly high fluidity.Appl..
Flexural Strength	92.0 MPa	13300 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP EP003 PEI LNP* Lubricomp EP003 is a Polyetherimide containing 15% PTFE/Silicone. Added features include: Internally Lubricated.
Flexural Strength	92.0 MPa	13300 psi	ISO 178
SABIC Innovative Plastics LNP Lubricomp LL003E PEEK LNP* Lubricomp* LL003E is a compound based on Polyetheretherketone (PEEK) containing PTFE. Characteristics of this grade are: Easy Molding and Internally Lubricated.This data was supplied by SABIC..
Flexural Strength	92.0 MPa	13300 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Xylex X7529 PC+POLYESTER (Asia Pacific) PC+ POLYESTER unreinforced alloy developed for optical or lense market. Good flow with good impact and excellent optical quality. UV 400nm block.This data was supplied by SABIC-IP for the Asia Pacif..
Flexural Strength	92.0 MPa	13300 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Xylex X7529 PC+POLYESTER (Europe-Africa-Middle East) PC+ POLYESTER unreinforced alloy developed for optical or lense market. Good flow with good impact and excellent optical quality. UV 400nm block.This data was supplied by SABIC-IP for the Europe-Afr..
Flexural Strength	92.0 MPa	13300 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Xylex X7529OQ PC+POLYESTER (Europe-Africa-Middle East) PC+ POLYESTER unreinforced alloy developed for optical or lense market. Good flow with good impact and excellent optical qualityThis data was supplied by SABIC-IP for the Europe-Africa-Middle East r..
Flexural Strength	92.0 MPa @Thickness 4.00 mm	13300 psi @Thickness 0.157 in	2.0 mm/min, Injection Molded; ISO 178
Styron EMERGEâ„¢ 7570 Polycarbonate (PC) / Acrylonitrile Butadiene Styrene (ABS) Overview: EMERGEâ„¢ PC/ABS 7570 Advanced Resin is a high flow, ignition-resistant PC/ABS blend that contains now chlorinated or brominated additives. Its superior processing makes it ideal for in..
Flexural Strength	92.0 MPa	13300 psi	ASTM D790
Plenco 2000 Phenolic, Granular, Compression Molded PLENCO 02000 is a versatile general purpose, organic filled phenolic molding compound, offering optimum cure characteristics and an excellent balance of molding properties. UL recognized under compo..
Flexural Strength	92.0 MPa	13300 psi	ASTM D790
Plenco 2311 Phenolic, Granular, Compression Molded PLENCO 02311 is a versatile general purpose organic filled phenolic molding compound offering excellent mold processability and optimized cure cycles. PLENCO 02311 is also granulated to provide impr..
Flexural Strength	92.0 MPa	13300 psi	ASTM D790
Plenco 4300 Phenolic, Granular, Transfer Molded PLENCO 04300 is a heat resistant, mineral filled phenolic molding compound offering optimum cure characteristics and excellent dimensional stability. It is formulated for wiring devices and electric..
Flexural Strength	92.0 MPa	13300 psi	2 mm/min; ISO 178
Chi Mei Kibisan® PN-106 L150 SAN High Clarity
Flexural Strength	92.0 MPa	13300 psi	2 mm/min; ISO 178
Chi Mei Kibisan® PN-107 L125 SAN High Clarity
Flexural Strength	92.0 MPa	13300 psi	ISO 178
Ascend Performance Materials Vydyne® ECO-315 Nylon 66/6, non-halogenated, ignition resistant, DAM Vydyne® ECO315 is non-halogenated, unfilled, flame-retardant PA66/6 copolymer with excellent strength and toughness. It is lubricated for machine feed and has an Underwriters Laboratories UL 94 fla..
Flexural Strength	92.0 MPa	13300 psi	2.6 mm/min; ASTM D790
BLUESTAR LXS 115 PPE-PS Typical Applications: Auto connect partsFire RatedInformation provided by Polymer Technology and Services, LLC (PTS).
Flexural Strength	92.0 MPa	13300 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Xylex X7529OQ PC+POLYESTER (Asia Pacific) PC+ POLYESTER unreinforced alloy developed for optical or lense market. Good flow with good impact and excellent optical qualityThis data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Strength	92.0 MPa	13300 psi	ISO 178
Polyplastics Duracon® HP25X Acetal Co-polymer (POM), High stiffness, High viscosity DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O)..