SABIC Innovative Plastics NORYL RN0712 PPE+HIPS (Asia Pacific)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL RN0712 PPE+HIPS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Noryl RN0712 is an unfilled Post Consumer recycle (PCR) based injection moldable modified polyphenylene ether resin comprising at least 37% PCR styrenic series resin content. Designed for good dimensional stability and high flow, this resin also uses non-chlorinated, non-brominated FR additives with a specific density of 1.1 g/cm^3. Noryl RN0712 may be an excellent material candidate for flat panel TV enclosure applications requiring good rheological properties, heat resistance, hydrolysis resistance and low density.
Physical Properties Metric English Comments
Density 1.11 g/cc
0.0401 lb/in³
ISO 1183
Viscosity 95000 cP
95000 cP
Melt Viscosity, 280°C, 1500 sec-1; ISO 11443
Melt Index of Compound 12 g/10 min

@Load 1.20 kg,
Temperature 280 °C
12 g/10 min

@Load 2.65 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
22 g/10 min

@Load 2.16 kg,
Temperature 280 °C
22 g/10 min

@Load 4.76 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 49.0 MPa
7110 psi
50 mm/min; ISO 527
50.0 MPa
7250 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 47.0 MPa
6820 psi
50 mm/min; ISO 527
51.0 MPa
7400 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 7.0 %
7.0 %
50 mm/min; ISO 527
10 %
10 %
SABIC - Japan Method
Elongation at Yield 3.0 %
3.0 %
50 mm/min; ISO 527
3.5 %
3.5 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.30 GPa
334 ksi
1 mm/min; ISO 527
2.47 GPa
358 ksi
50 mm/min; ASTM D638
Flexural Strength 82.0 MPa
11900 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Yield Strength 77.0 MPa
11200 psi
2 mm/min; ISO 178
Flexural Modulus 2.25 GPa
326 ksi
2 mm/min; ISO 178
2.30 GPa
334 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.490 J/cm

@Thickness 6.40 mm
0.918 ft-lb/in

@Thickness 0.252 in
ASTM D256
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
4.00 kJ/m²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.300 J/cm²

@Temperature -30.0 °C
1.43 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 74.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
74.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.1 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 87.0 °C
189 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
Vicat Softening Point 110 °C
230 °F
Rate B/50; ISO 306
110 °C
230 °F
Rate B/50; ASTM D1525
112 °C
234 °F
Rate B/120; ISO 306
Flammability, UL94 V-1

@Thickness 1.50 mm
V-1

@Thickness 0.0591 in
UL 94
Oxygen Index 34 %
34 %
ISO 4589
Glow Wire Test 725 °C
1340 °F
IEC 60695-2-13
725 °C
1340 °F
IEC 60695-2-13
725 °C
1340 °F
IEC 60695-2-13
960 °C

@Thickness 1.00 mm
1760 °F

@Thickness 0.0394 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
1.00e+16 ohm-cm
1.00e+16 ohm-cm
IEC 60093
Dielectric Constant 2.9

@Frequency 1.00e+6 Hz
2.9

@Frequency 1.00e+6 Hz
IEC 60250
2.91

@Frequency 1.00e+6 Hz
2.91

@Frequency 1.00e+6 Hz
ASTM D150
2.91

@Frequency 1.00e+6 Hz
2.91

@Frequency 1.00e+6 Hz
ASTM D150
Dissipation Factor 0.0032

@Frequency 1.00e+6 Hz
0.0032

@Frequency 1.00e+6 Hz
ASTM D150
0.0032

@Frequency 1.00e+6 Hz
0.0032

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 175 - 250 V
175 - 250 V
UL 746A