- Beijing Chemical Industry KAIFA® MN301-G0 Nylon 66 Resin
Beijing Chemical Industry KAIFA® MN301-G0 Nylon 66 Resin
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant |
| Manufacturer | Beijing Chemical Industry Research Institute (Group) |
| Trade Name | KAIFA® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Beijing Chemical Industry KAIFA® MN301-G0 Nylon 66 Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High flame retardant, Good flowInformation provided by Beijing Chemical Industry Research Institute (Group)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 - 0.014 cm/cm | 0.0070 - 0.014 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ASTM D638 |
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO179 |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.7 @Frequency 1e+6 Hz |
2.7 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 26.0 kV/mm @Thickness 2.00 mm |
660 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 220 - 265 °C | 428 - 509 °F | |
| Middle Barrel Temperature | 260 - 265 °C | 500 - 509 °F | |
| Front Barrel Temperature | 260 - 270 °C | 500 - 518 °F | |
| Nozzle Temperature | 260 - 265 °C | 500 - 509 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 60.0 - 100 MPa | 8700 - 14500 psi |
Users viewing this material also viewed the following:
- ICO Polymers ICOFLOâ„¢ 510-5072 1200 Micron LLDPE Powder
- Lehmann & Voss LUVOCOM® 1105/GF/30/BK-1 PEEK, with glass fiber
- A. Schulman POLYBATCH™ White 8153/UV2 Concentrate Based In Polyethylene
- Tra-Con Tra-Duct 29121 Snap Cure Conductive Silver Epoxy Adhesive
- TPI Porene® ABS-GA803 High Gloss, UV Resistant ABS Resin
- Chosun Refractories INCT-120N Light-Weight Castable
- 3M FL010008 Lexan Label Product
- BASF Ultramid® A3Z HP UV PA66 (Dry)
- A. Schulman ComAlloy Hiloy® 283 PPO Alloy, Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved