SABIC Innovative Plastics LNP LUBRILOY R2000 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Lubriloy |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRILOY R2000 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRILOY* R2000 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ASTM D792 |
| 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.250 % | 0.250 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.018 - 0.022 cm/cm @Time 86400 sec |
0.018 - 0.022 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.021 - 0.031 cm/cm @Time 86400 sec |
0.021 - 0.031 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 53.0 MPa | 7690 psi | ISO 527 |
| 55.0 MPa | 7980 psi | ASTM D638 | |
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | ASTM D638 |
| Elongation at Break | 27 % | 27 % | ASTM D638 |
| 32.3 % | 32.3 % | ISO 527 | |
| Elongation at Yield | 14 % | 14 % | ASTM D638 |
| Tensile Modulus | 2.41 GPa | 350 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 65.0 MPa | 9430 psi | ISO 178 |
| 82.0 MPa | 11900 psi | ASTM D790 | |
| Flexural Modulus | 2.00 GPa | 290 ksi | ISO 178 |
| 2.31 GPa | 335 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.620 J/cm | 1.16 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 17.24 J/cm | 32.30 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 141 kJ/m² | 67.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.36 | 0.36 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.27 | 0.27 | ASTM D3702 Modified |
| K (wear) Factor | 101 x 10-8 mm³/N-M | 50.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 77.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
43.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 103 µm/m-°C @Temperature -40.0 - 40.0 °C |
57.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 77.0 °C @Thickness 3.20 mm |
171 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Northstar Polymers MPP-D65A Polyether Base Polyurethane Resin
- H.C. Starck FeNiCo Atomized Powder
- A. Schulman POLYFLAM™ RCP 770C/CW
- DuPont Bynel® 3860 Anhydride-Modified Ethylene Vinyl Acetate Adhesive Resin
- Zeon Chemicals Hydrin® H1100 Polyepichlorohydrin Elastomer
- Zhejiang Juner 201-G20 20% Glass Fibre Reinforced
- A. Schulman POLYBLAK™ 4642 Premium Black Color Concentrate, 40% Carbon Black Based In LLDPE
- AK Steel 430 ULTRA FORM® Stainless Steel
- Solvay Specialty Polymers Veradel® AG-330 Polyethersulfone (PESU) (Unverified Data**)
- ELASTO UK Dryflex® 600500S SEBS Based Material, Filled Qualities, 50A Hardness, Natural
Copyright © lookpolymers.com All Rights Reserved