BASF Ultramid® B3WG10 BK 00564 50% Glass Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® B3WG10 BK 00564 50% Glass Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: 50% glass-fiber reinforced and heat aging resistant injection-molding grade for technical parts with very high stiffness.Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.500 - 0.800 g/cc
0.0181 - 0.0289 lb/in³
Density 1.55 g/cc
0.0560 lb/in³
ISO 1183
Water Absorption 4.5 - 5.1 %
4.5 - 5.1 %
Saturation; ISO 62
Moisture Absorption at Equilibrium 1.3 - 1.7 %
1.3 - 1.7 %
23°C; 50% RH; ISO 62
Viscosity Measurement 135
135
ISO 307
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
restricted
Melt Flow 38.75 g/10 min

@Load 5.00 kg,
Temperature 275 °C
 38.75 g/10 min

@Load 11.0 lb,
Temperature 527 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 225 MPa
32600 psi
50 mm/min; ISO 527-1/-2
Elongation at Yield 2.5 %
2.5 %
50 mm/min; ISO 527-1/-2
Modulus of Elasticity 16.7 GPa
2420 ksi
ISO 527-1/-2
Flexural Strength 345 MPa
50000 psi
at max force; ISO 178
Flexural Modulus 14.5 GPa
2100 ksi
ISO 178
Izod Impact, Notched (ISO) 20.0 kJ/m²

@Temperature 23.0 °C
 9.52 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/A
Charpy Impact Unnotched 8.80 J/cm²

@Temperature -30.0 °C
 41.9 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
9.00 J/cm²

@Temperature 23.0 °C
 42.8 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 1.40 J/cm²

@Temperature -30.0 °C
 6.66 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
1.90 J/cm²

@Temperature 23.0 °C
 9.04 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 10.0 - 15.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 5.56 - 8.33 µin/in-°F

@Temperature 73.4 - 176 °F
 DIN 11359-1/-2
CTE, linear, Transverse to Flow 50.0 - 60.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 27.8 - 33.3 µin/in-°F

@Temperature 73.4 - 176 °F
 DIN 11359-1/-2
Specific Heat Capacity 1.30 J/g-°C
0.311 BTU/lb-°F
Thermal Conductivity 0.380 W/m-K
2.64 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 220 °C
428 °F
DIN 53765
Maximum Service Temperature, Air 145 °C
293 °F
for 50% loss of tensile strength after 20000hr
175 °C
347 °F
for 50% loss of tensile strength after 5000hr
200 °C
392 °F
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 215 °C
419 °F
ISO 75-1/-2
Decomposition Temperature >= 300 °C
>= 572 °F
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 4.2

@Frequency 1.00 Hz
 4.2

@Frequency 1.00 Hz
 IEC 60250
Dissipation Factor 0.014

@Frequency 1.00e+6 Hz
 0.014

@Frequency 1.00e+6 Hz
 IEC 60250
Processing Properties Metric English Comments
Processing Temperature 80.0 °C
176 °F
Hopper Throat
Zone 1 270 °C
518 °F
Feed Zone
Zone 2 280 °C
536 °F
Compression
Zone 3 290 °C
554 °F
Metering-zone
Zone 4 290 °C
554 °F
Nozzle
Melt Temperature 290 °C
554 °F
Optimal
280 - 300 °C
536 - 572 °F
Injection-molding/Extrusion
Mold Temperature 80.0 °C
176 °F
Optimal
80.0 - 90.0 °C
176 - 194 °F
Injection-molding
Drying Temperature 80.0 °C
176 °F
Dry Time 4 hour
4 hour
Moisture Content 0.030 - 0.060 %
0.030 - 0.060 %
Optimal
<= 0.15 %
<= 0.15 %
Descriptive Properties Value Comments
Color BK 00564
Commercial Status Europe
Ignition Temperature >400°C
ASTM D129
Peripheral screw speed < 0.3 m/s