Vyncolit 4523 XB Novolac Phenolic

Category	Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic
Manufacturer	Vyncolit N.V., Sumitomo Bakelite
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Vyncolit 4523 XB Novolac Phenolic.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Organic and inorganic filled phenolic molding compound with good mechanical and thermal properties. Improved heat resistance compared to organic filled compounds.USES: Fuse holders, brush holders, circuit breakers, automotive ignition and solenoid covers.Information provided by Vyncolit, a Sumitomo Bak Group

Physical Properties	Metric	English	Comments
Bulk Density	0.700 g/cc	0.0253 lb/in³	Powder Density; ISO 60
Density	1.60 g/cc	0.0578 lb/in³	Relative Density; ISO 1183
Linear Mold Shrinkage	0.0090 cm/cm	0.0090 in/in	Injection Molding; ISO 2577

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	50.0 MPa	7250 psi	ISO 527
Elongation at Break	0.60 %	0.60 %	Tensile; ISO 527
	1.5 %	1.5 %	Flexure; ISO 178
Tensile Modulus	10.0 GPa	1450 ksi	ISO 527
Flexural Strength	95.0 MPa	13800 psi	At Rupture; ISO 178
Flexural Modulus	9.50 GPa	1380 ksi	ISO 178
Compressive Strength	200 MPa	29000 psi	ISO 604
Charpy Impact Unnotched	0.700 J/cm²	3.33 ft-lb/in²	ISO 179
Charpy Impact, Notched	0.200 J/cm²	0.952 ft-lb/in²	ISO 179

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	50.0 µm/m-°C @Temperature 20.0 °C	27.8 µin/in-°F @Temperature 68.0 °F	TMA
CTE, linear, Transverse to Flow	60.0 µm/m-°C @Temperature 20.0 °C	33.3 µin/in-°F @Temperature 68.0 °F	TMA
Deflection Temperature at 1.8 MPa (264 psi)	175 °C	347 °F	ISO 75 Af
Flammability, UL94	V-1 @Thickness 1.60 mm	V-1 @Thickness 0.0630 in
	V-0 @Thickness 4.00 mm	V-0 @Thickness 0.157 in
Shrinkage	0.35 %	0.35 %	Post Shrinkage; ISO 2577

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+14 ohm-cm	1.00e+14 ohm-cm	DIN 53482
Surface Resistance	1.00e+12 ohm	1.00e+12 ohm	IEC 93
Insulation Resistance	1.00e+10 ohm	1.00e+10 ohm	Dry; IEC 167
	1.00e+10 ohm	1.00e+10 ohm	Wet; 24 hours in water; IEC 167
Dielectric Strength	25.0 kV/mm	635 kV/in	IEC 243
Comparative Tracking Index	175 V	175 V	IEC 112

Descriptive Properties	Value	Comments
Color	Black
ISO type	PF 2 C3
Main Filler	Organic & Inorganic
Molding Method	Compression, transfer, injection