Asia International Enterprise (Hong Kong) 60G5 Nylon 66, 25% Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Asia Int'l Enterprise (Hong Kong) Limited |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asia International Enterprise (Hong Kong) 60G5 Nylon 66, 25% Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asia International Enterprise (Hong Kong) Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.37 g/cc @Temperature 23.0 °C |
1.37 g/cc @Temperature 73.4 °F |
ASTM D792 |
| Filler Content | 25 % | 25 % | |
| Linear Mold Shrinkage | 0.0040 - 0.0090 cm/cm | 0.0040 - 0.0090 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Ultimate | 167 MPa | 24200 psi | 5mm/min; ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | 5mm/min; ASTM D638 |
| Flexural Strength | 245 MPa | 35500 psi | 2.8mm/min; ASTM D790 |
| Flexural Modulus | 7.85 GPa | 1140 ksi | 2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 0.981 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
1.84 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 261 °C | 502 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 250 - 300 °C | 482 - 572 °F | Cylinder Temperature |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour |
Users viewing this material also viewed the following:
- LG Chemical Lupoy NF1009F 15 Polycarbonate Resin
- SABIC Innovative Plastics LNP LUBRICOMP RA004 PA 66 (Asia Pacific)
- Samsung Cheil Industries Starex® VE-0856 (VE-0856U UV) Flame Retardant Grade ABS
- Zircar Ceramics ECO-1200B Alumina-Silica Insulation
- Dow Corning 2-3912 Antifoam
- Clariant Renol PEEKSP0002 Polyetheretherketone, 30% Glass Fiber
- A. Schulman POLYBLAK™ 4651SF Universal Black Color Concentrate, 50% Carbon Black in EVA
- Albis Plastics Cellulose Acetate Butyrate B902 (UV Inhibitor Added), 16% Plasticizer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved