SABIC Innovative Plastics LNP LUBRICOMP PL002 PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP PL002 PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* PL002 is a compound based on Nylon 6 base resin containing 10% PTFE. Added feature of this grade is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 52.0 MPa | 7540 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 25 % | 25 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 3.73 GPa | 541 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 78.0 MPa | 11300 psi | ISO 178 |
| Flexural Modulus | 2.14 GPa | 310 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 0.470 J/cm | 0.881 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.7 J/cm | 21.9 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 67.0 kJ/m² | 31.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J @Temperature 23.0 °C |
6.64 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 24.0 J | 17.7 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.60 | 0.60 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.42 | 0.42 | ASTM D3702 Modified |
| K (wear) Factor | 149 x 10-8 mm³/N-M | 74.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 96.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
53.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 95.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
52.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 133 °C | 271 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 144 °C @Thickness 3.20 mm |
291 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 51.0 °C | 124 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 54.0 °C @Thickness 3.20 mm |
129 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers GA-509OR PVC
- Plastcom SLOVASTER® B1 GF 20 000/1 PBT, 20% glass fibre
- LG Chemical HG193S ABS, High Flow, Chemical Resistance
- KKPC KOSYN KSL 611 Styrene-Butadiene Latex
- Karina E 5525/1-TRE Kariprene Natural.
- Eastman Tenite 285E3720005 Butyrate Clear, Trsp
- ExxonMobil Exxtral™ LNV 010 Performance Polyolefin
- Cyclewood Solutions Xylomer™ XM1-GQD Compostable Film Resin
- Diamond Polymers ABS 4000HH-ELG
- Carpenter BioDur™ CCM Plus™ Medical Implant Alloy, Annealed 1093°C 2 hr
Copyright © lookpolymers.com All Rights Reserved