- DuPont Performance Polymers Delrin® 100TL NC010 Acetal Homopolymer (Unverified Data**)
DuPont Performance Polymers Delrin® 100TL NC010 Acetal Homopolymer (Unverified Data**)
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, PTFE-Filled |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Delrin® 100TL NC010 Acetal Homopolymer
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Delrin® 100TL NC010 is a high viscosity acetal homopolymer with 1.5% Teflon® PTFE Micropowder.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.018 cm/cm @Thickness 2.00 mm |
0.018 in/in @Thickness 0.0787 in |
ISO 294-4 |
| 0.019 cm/cm @Thickness 4.00 mm |
0.019 in/in @Thickness 0.157 in |
||
| Linear Mold Shrinkage, Transverse | 0.017 cm/cm @Thickness 2.00 mm |
0.017 in/in @Thickness 0.0787 in |
ISO 294-4 |
| Melt Flow | 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 71.0 MPa @Temperature 23.0 °C |
10300 psi @Temperature 73.4 °F |
ISO 527 |
| Elongation at Break | 33 % @Temperature 23.0 °C |
33 % @Temperature 73.4 °F |
nominal; ISO 527 |
| Elongation at Yield | 25 % @Temperature 23.0 °C |
25 % @Temperature 73.4 °F |
ISO 527 |
| Tensile Modulus | 3.00 GPa @Temperature 23.0 °C |
435 ksi @Temperature 73.4 °F |
ISO 527 |
| Flexural Modulus | 2.80 GPa @Temperature 23.0 °C |
406 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact Unnotched | 15.0 J/cm² @Temperature 23.0 °C |
71.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 0.800 J/cm² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.900 J/cm² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature -40.0 - 23.0 °C |
278 µin/in-°F @Temperature -40.0 - 73.4 °F |
ISO 11359-1/-2 |
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1/-2 | |
| 500 µm/m-°C @Temperature 55.0 - 100 °C |
278 µin/in-°F @Temperature 131 - 212 °F |
ISO 11359-1/-2 | |
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature -40.0 - 23.0 °C |
55.6 µin/in-°F @Temperature -40.0 - 73.4 °F |
ISO 11359-1/-2 |
| 110 µm/m-°C @Temperature 23.0 - 55.0 °C |
61.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1/-2 | |
| 160 µm/m-°C @Temperature 55.0 - 100 °C |
88.9 µin/in-°F @Temperature 131 - 212 °F |
ISO 11359-1/-2 | |
| Melting Point | 178 °C | 352 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 158 °C | 316 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO 75-1/-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 215 °C | 419 °F | Optimum; Injection Molding |
| 210 - 220 °C | 410 - 428 °F | Injection Molding | |
| Mold Temperature | 90.0 °C | 194 °F | optimum; Injection Molding |
| 80.0 - 100 °C | 176 - 212 °F | Injection Molding | |
| Drying Temperature | 80.0 °C | 176 °F | Injection Molding |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Injection Molding |
| Moisture Content | <= 0.20 % | <= 0.20 % | Injection Molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Lubricant, PTFE | |
| Appearance | Natural Color | |
| Features | Creep Resistance, Good | |
| Dimensional Stability, Good | ||
| Friction, Low | ||
| Homopolymer | ||
| Molecular Wt., High | ||
| Stiffness, High | ||
| Strength, High | ||
| Viscosity, High | ||
| Wear Resistance, Good | ||
| Forms | Pellets | |
| Generic | Acetal (POM) Homopolymer | |
| Material Status | Preliminary Data | |
| Part Marking Code | >POM-SD< | ISO 11469 |
| Polymer Family | POM | |
| Polymer Type | POM Homopolymer | |
| Processing Method | Extrusion | |
| Injection Molding | ||
| Product Category | Extrusion Resins | |
| Low Wear and Friction Resins | ||
| Unreinforced Resins | ||
| Region Available - Global | Yes | |
| Resin Identification | POM-SD | ISO 1043 |
| RoHS Compliance | Contact Manufacturer | |
| Uses | Conveyors | |
| Gears | ||
| Parts, Engineering | ||
| Tubing |
Users viewing this material also viewed the following:
- RheTech Products T10P100-01 10% Talc Reinforced Polypropylene, Black
- SABIC Innovative Plastics Cycolac® GPM5500U ABS (Europe-Africa-Middle East)
- NOVA Chemicals Dylark® 432 High-Heat Styrenic Copolymer
- RheTech Products HP522-473 15% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, ZU5A Dark Graphite
- Materion AMC225XE T4 Aluminum/Silicon Carbide MMC Extruded Bar
- Haynes 214® alloy, 50% cold reduction
- Haysite 44500 Vinyl Ester SMC, 30% Glass Reinforced
- Heatbath/Park Marquench Quenching and Tempering Salt
- Tra-Con Tra-Bond 342-3.5 Room Temperature Cure Epoxy Adhesive
- Dow DNDA-7147 NT 7 Linear Low Density Polyethylene Resin
Copyright © lookpolymers.com All Rights Reserved