PolyOne Geon™ Vinyl Rigid Extrusion 78761 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Extrusion 78761 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Note: NSF listings are obtained on specific colors. Contact PolyOne for the latest listing of approved colors for this product.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 80 | 80 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 50.3 MPa | 7300 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.83 GPa | 410 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 103 MPa | 14900 psi | ASTM D790 |
| Flexural Modulus | 2.90 GPa | 421 ksi | ASTM D790 |
| Izod Impact, Notched | 0.480 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
0.899 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Flow; ASTM D256A |
| 0.530 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
0.993 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Across Flow; ASTM D256A | |
| Dart Drop Total Energy | 62.3 J/cm @Temperature 23.0 °C |
0.117 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| 145 J/cm @Temperature 23.0 °C |
0.272 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 52.0 µm/m-°C | 28.9 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C @Thickness 3.18 mm |
158 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.91 mm |
V-0 @Thickness 0.0752 in |
ALL; UL 94 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 193 °C | 360 - 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Agency Ratings | NSF 14 | |
| NSF 61 | ||
| NSF Type I | ||
| Ease of Sizing | Good | |
| Features | Good Chemical Resistance | |
| Forms | Cube | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Extrusion | |
| PVC Cell Classification | 12454 | ASTM D1784 |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Rods |
Users viewing this material also viewed the following:
- MV Labs IN500 InF3 Indium(III) fluoride
- DuPont™ Surlyn® 1601B Sodium Ionomer Resin for Blown and Cast Film (discontinued **)
- Chesterton 438 PTFE Coating
- DuPont Performance Polymers Neoprene WHV Polychloroprene Rubber
- Arlon 55581R028 0.028" (0.711 mm) Uncured Silicone Rubber with Fiberglass Substrate
- 3M FA021 Matte Clear Acetate Label Products
- Weartech International WT-12H Cobalt Hardfacing & Wear Resistant Alloy
- Gwent Electronic Materials C2080815P1 Silver Flexographic Ink
- Permabond A905 Anaerobic Surface Activator
Copyright © lookpolymers.com All Rights Reserved