Asahi Kasei Xyron® 220Z Modified Polyphenylene Ether
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Heat Resistant |
| Manufacturer | Asahi Kasei |
| Trade Name | Xyron® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Xyron® 220Z Modified Polyphenylene Ether.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame RetardantInformation provided by Asahi Kasei
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | 23°C; ASTM D792 |
| Moisture Absorption | 0.100 % | 0.100 % | 23°C, 50% RH 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | 23°C, 50% RH; ASTM D638 |
| Elongation at Break | 50 % | 50 % | 23°C, 50% RH; ASTM D638 |
| Flexural Strength | 69.0 MPa | 10000 psi | 23°C, 50% RH; ASTM D790 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 23°C, 50% RH; ASTM D790 |
| Izod Impact, Notched | 1.47 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
2.75 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| 2.16 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
4.05 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C @Temperature -30.0 - 60.0 °C |
44.4 µin/in-°F @Temperature -22.0 - 140 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | 50% RH; ASTM D257 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | 50% RH; ASTM D257 |
| Dielectric Constant | 2.9 @Frequency 1e+6 Hz |
2.9 @Frequency 1e+6 Hz |
3.0 mm 5VA; ASTM D150 |
| 2.9 @Frequency 1e+6 Hz |
2.9 @Frequency 1e+6 Hz |
50% RH; ASTM D150 | |
| Dielectric Strength | 29.0 kV/mm @Thickness 2.00 mm |
737 kV/in @Thickness 0.0787 in |
Short time; ASTM D149 |
| Dissipation Factor | 0.0030 @Frequency 60 Hz |
0.0030 @Frequency 60 Hz |
50% RH; ASTM D150 |
| 0.0040 @Frequency 1e+6 Hz |
0.0040 @Frequency 1e+6 Hz |
50% RH; ASTM D150 | |
| Arc Resistance | 80 sec | 80 sec | Tungsten; ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 220 - 270 °C | 428 - 518 °F | Resin Temperature |
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F | |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Pre-drying Temperature |
| Dry Time | 2 - 4 hour | 2 - 4 hour |
Users viewing this material also viewed the following:
- Hogen Duralloy H20TC 70 Tungsten Carbide/30 Copper PM Metal Composite
- Industeel CLC 17.12.2 L 2% Mo Containing 18 Cr –10 Ni Austenitic Stainless Steel
- Momentive Performance Materials Siloprenâ„¢ LIM 6041 Liquid Silicone Rubber - Healthcare Radio Opaque (X-Ray Detectability)
- Samsung Cheil Industries Starex® BF-0370 MABS, Unreinforced Scratch Resistant
- Dow Corning SILASTIC® 24043-V SILICONE RUBBER BLUE
- ChevronTexaco Starplex® Moly NLGI Grade 1
- Eurotec® Tecomid® NB30 GR15 BK005 FS90 PA6, 15% glass fiber reinforced, flame retardant - halogen & red phosphorus free, low smoke & toxic gas grade
- Azoty Tarnow™ Alphalon™ 27 Nylon 6
- Beijing Evergrow Resources UHF-R2400 UHMW PE Fiber
Copyright © lookpolymers.com All Rights Reserved