- Arlon 51586R040 0.040" (1.02 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Arlon 51586R040 0.040" (1.02 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
| Category | Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon 51586R040 0.040" (1.02 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Design/Construction:Side 1: Cured Silicone RubberSide 2: Uncured Silicone RubberAppearance: Red silicone gum and rubber on fiberglass clothThis data Represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Thickness | 76.2 microns | 3.00 mil | Polyethylene, Interleave |
| >= 102 microns | >= 4.00 mil | Side 1 | |
| 203 microns | 8.00 mil | Prime Coated 7628 Fiberglass, Substrate | |
| >= 635 microns | >= 25.0 mil | Side 2 | |
| 965 - 1070 microns | 38.0 - 42.0 mil | Overall |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 40 - 50 | 40 - 50 | Compound Property |
| Tensile Strength | >= 5.52 MPa | >= 800 psi | Compound Property |
| Elongation at Break | 500 % | 500 % | Compound Property |
| Peel Strength | >= 1.05 kN/m | >= 6.00 pli | Bond Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 200 °C | 392 °F | rated per UL card E54153 |
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |
| Flammability, UL94 | HB | HB | Compound Rated |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | >= 15.7 kV/mm | >= 400 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Postcure Cycle |
| 15.0 min @Pressure 0.345 MPa, Temperature 135 °C |
0.250 hour @Pressure 50.0 psi, Temperature 275 °F |
Recommended Cure Cycle | |
| Shelf Life | 6.00 Month @Temperature 23.9 °C |
6.00 Month @Temperature 75.0 °F |
From date of manufacture |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Red | |
| Total Product Weight (oz/yd2) | 61.4 - 67.4 | |
| Uncoated Fabric Break Strength | 200 lb/in | Fill Direction, Substrate Property |
| 250 lb/in | Warp Direction, Substrate Property |
Users viewing this material also viewed the following:
- PolyOne OnFlex™ S EF 80A-3S1977 Thermoplastic Elastomer (TPE)
- Mitsui ADMER® QF551A PP Type Polyolefin
- SCG Chemicals EL-Leneâ„¢ L1810F Linear Low Density Polyethylene Film
- Teknor Apex Sinpolene MBW1475 Specialty Polystyrene
- A. Schulman PP 1116-01 Polypropylene Molding Grade Copolymer Polypropylene
- A. Schulman POLYBATCH™ Hot Pink 50377 Concentrate Based In Polyethylene
- Washington Penn Homopolymer Polypropylene 30% Calcium Carbonate Filled
- ExxonMobil Exceed™ 1018LA Metallocene Polyethylene Resin (Asia Pacific Grade)
- Arlon 51601W015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Karina E 841-08/184-A-ERYB Beige PVC Compound
Copyright © lookpolymers.com All Rights Reserved