A. Schulman ComAlloy Hiloy® 102 Polypropylene, Glass Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | A. Schulman ComAlloy |
| Trade Name | Hiloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman ComAlloy Hiloy® 102 Polypropylene, Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 99 | 99 | ASTM D785 |
| Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
| Elongation at Break | 4.2 % | 4.2 % | ASTM D638 |
| Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.20 J/cm | 5.99 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 164 °C | 327 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 116 °C | 241 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 229 - 246 °C | 444 - 475 °F |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 223R PC (Asia Pacific)
- Loxim 820 02C HB Polypropylene Compound, 20% Calcite Filled, Flame Retardant
- Isoflon PVC Polyvinyl Chloride
- Borealis FR4830 Chemically Crosslinkable Polyethylene Compound for Primary Automotive Wires
- Master Bond Supreme 46HT-2 Toughened, High Shear and Peel Strength Adhesive
- A. Schulman POLYFLAM™ RCP 770C/CW
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with Plasthall 7050
- A. Schulman PAPERMATCH® H-5338 Specialty Masterbatch
- Arlon 30400N125 0.125" (3.17 mm) Uncured, Unsupported Silicone Rubber on a Kodacel Carrier
Copyright © lookpolymers.com All Rights Reserved