- Arlon 51576R027 0.027" (0.686 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Arlon 51576R027 0.027" (0.686 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
| Category | Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon 51576R027 0.027" (0.686 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Design/Construction: Interleave: Polyethylene Side 1: Cured Silicone RubberSubstrate: 7628 Style Fiberglass Side 2: Uncured Silicone Rubber This data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Thickness | 76.2 microns | 3.00 mil | Interleave |
| 102 microns | 4.00 mil | Side 1 | |
| 203 microns | 8.00 mil | Substrate | |
| >= 330 microns | >= 13.0 mil | Side 2 | |
| 622 - 749 microns | 24.5 - 29.5 mil | Overall |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 40 - 50 | 40 - 50 | Compound Property |
| Tensile Strength | >= 5.52 MPa | >= 800 psi | Compound Property |
| Elongation at Break | >= 500 % | >= 500 % | Compound Property |
| Peel Strength | >= 1.05 kN/m | >= 6.00 pli | Bond Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 232 °C | 450 °F | |
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |
| UL RTI, Electrical | 220 °C | 428 °F | per card E54153 |
| UL RTI, Mechanical without Impact | 200 °C | 392 °F | per card E54153 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | >= 15.7 kV/mm | >= 400 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Postcure Cycle |
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle | |
| Shelf Life | 6.00 Month @Temperature 23.9 °C |
6.00 Month @Temperature 75.0 °F |
From date of manufacture |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Red | |
| Total Product Weight (oz/yd2) | 24.4 - 29.4 | |
| Uncoated Fabric Break Strength | 200 lb/in | Fill Direction, Substrate Property |
| 250 lb/in | Warp Direction, Substrate Property |
Users viewing this material also viewed the following:
- Solvay TECHNYL® C 218 V 30 PA6, 30% glass fiber, Conditioned
- Schwartz Technical Plastics MITELA® 2/5 A Cotton Fabric, Special Quality
- A. Schulman POLYBATCH™ CE-505-B Concentrate Based In Polyethylene
- Eagle Brass 521 Phosphor Bronzes 8% C, Hard
- DuPont Teijin Films Mylar® OB13AF Polyester Film, 150 Gauge
- Arlon 56606R026M 0.026" (0.660 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Asahi Glass Fluon® P-805UP PFA Perfluoropolymer
- Azdel SuperLite® SL551400-100 PP Resin Matrix / 55% Glass Fiber (4 mm Molded Thickness)
Copyright © lookpolymers.com All Rights Reserved