Arlon 51576R024A 0.024" (0.610 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
| Category | Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon 51576R024A 0.024" (0.610 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Design/Construction: Interleave: Polyethylene Side 1: Cured Silicone RubberSubstrate: 7628 Style Fiberglass Side 2: Uncured Silicone Rubber This data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | Silicone Property; Arlon SQA-TMS-024 |
| Thickness | 76.2 microns | 3.00 mil | Interleave |
| 203 microns | 8.00 mil | Side 1; Arlon SQA-TMS-003 | |
| 203 microns | 8.00 mil | Side 2; Arlon SQA-TMS-003 | |
| 203 microns | 8.00 mil | Substrate; Arlon SQA-TMS-003 | |
| 610 microns | 24.0 mil | Overall; Arlon SQA-TMS-003 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 45 | 45 | Silicone Property; ASTM D2240 |
| Tensile Strength | 6.21 MPa | 900 psi | Silicone Property; ASTM D412 |
| Elongation at Break | 400 % | 400 % | Silicone Property; ASTM D412 |
| Peel Strength | 1.58 kN/m | 9.00 pli | Bond Strength; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 232 °C | 450 °F | |
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |
| UL RTI, Electrical | 220 °C | 428 °F | |
| UL RTI, Mechanical without Impact | 200 °C | 392 °F | |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 15.7 kV/mm | 400 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Postcure Cycle |
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle | |
| Shelf Life | 6.00 Month @Temperature 23.9 °C |
6.00 Month @Temperature 75.0 °F |
From date of manufacture |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Red | |
| Total Product Weight (oz/yd2) | 29.9 | Arlon SQA-TMS-025 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable W1200 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Plastcom PLASTAMID® 610 BT N 32 C PA610
- Eastman Eastapak 9921W PET (discontinued **)
- TSE Industries Millathane® 28 Millable Polyester Polyurethane Rubber
- Solvay ANTAROX® BL 225 E Surfactant
- SABIC Innovative Plastics LNP THERMOCOMP MFB82I PP (Europe-Africa-Middle East)
- EMS-Grivory Grivory® XE 4120 black 9916 PA*-GF30
- Bond Laminates TEPEX® dynalite 102-RGUD600(x)/47% Roving Glass – PA 6 Consolidated Composite Laminate
- Arlon Thermabond® 48781A008 0.008" (0.203 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved