Arkema Group Orgalloy® RS 6600 Polyamide 6.6 Alloy

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer Arkema
Trade Name Orgalloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Orgalloy® RS 6600 Polyamide 6.6 Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide Alloy, Rigid grade, Nylon 6.6 basedTubes / Mandrels / Profiles / CablesInformation provided by Arkema Group
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ISO R1183
Water Absorption 0.70 %
0.70 %
23°C / 24 hrs; ISO 62
Moisture Absorption at Equilibrium 1.2 %
1.2 %
23°C / 50% RH; ISO 62
2.9 %
2.9 %
in 23°C water; ISO 62
Melt Flow 15 g/10 min

@Load 2.16 kg,
Temperature 235 °C
 15 g/10 min

@Load 4.76 lb,
Temperature 455 °F
 after drying; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 77
77
ISO 868
Tensile Strength, Ultimate 50.0 MPa
7250 psi
ISO R527
Tensile Strength, Yield 51.5 MPa
7470 psi
ISO R527
Elongation at Break >= 100 %
>= 100 %
ISO R527
Elongation at Yield 4.1 %
4.1 %
ISO R527
Modulus of Elasticity 2.60 GPa
377 ksi
ISO R527
Flexural Strength 67.0 MPa
9720 psi
After conditioning at 23°C and 50% RH; ISO 178
75.0 MPa
10900 psi
Dry; ISO 178
Flexural Modulus 2.10 GPa
305 ksi
After conditioning at 23°C and 50% RH; ISO 178
2.30 GPa
334 ksi
Dry; ISO 178
Charpy Impact, Notched 2.00 J/cm²
9.52 ft-lb/in²
After conditioning at 23°C/50%RH; ISO 179/Af
1.20 J/cm²

@Temperature -20.0 °C
 5.71 ft-lb/in²

@Temperature -4.00 °F
 Dry; ISO 179/Af
1.30 J/cm²

@Temperature -20.0 °C
 6.19 ft-lb/in²

@Temperature -4.00 °F
 After conditioning at 23°C/50%RH; ISO 179/Af
1.70 J/cm²

@Temperature 23.0 °C
 8.09 ft-lb/in²

@Temperature 73.4 °F
 Dry; ISO 179/Af
Tensile Creep Modulus, 1 hour 2270 MPa
329000 psi
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear 65.0 µm/m-°C

@Temperature 20.0 - 60.0 °C
 36.1 µin/in-°F

@Temperature 68.0 - 140 °F
 TMS2 Perkin Elmer
CTE, linear, Transverse to Flow 110 µm/m-°C

@Temperature 20.0 - 60.0 °C
 61.1 µin/in-°F

@Temperature 68.0 - 140 °F
 TMS2 Perkin Elmer
Melting Point 255 °C
491 °F
ISO R1218
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
320 °F
ISO R75
Deflection Temperature at 1.8 MPa (264 psi) 80.0 °C
176 °F
ISO R75
Vicat Softening Point 165 °C
329 °F
50 N - B method; ISO 306
225 °C
437 °F
10 N - A method; ISO 306
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Volume Resistivity 6.00e+15 ohm-cm
6.00e+15 ohm-cm
ASTM D257
Surface Resistance 2.50e+16 ohm
2.50e+16 ohm
ASTM D257
Dielectric Strength 36.0 kV/mm

@Thickness 1.00 mm
 914 kV/in

@Thickness 0.0394 in
 ASTM D149
Dissipation Factor 0.017

@Frequency 100000 Hz
 0.017

@Frequency 100000 Hz
 NFC 26 230
0.025

@Frequency 100 Hz
 0.025

@Frequency 100 Hz
 NFC 26 230
0.032

@Frequency 1000 Hz
 0.032

@Frequency 1000 Hz
 NFC 26 230
Comparative Tracking Index >= 600 V
>= 600 V
NFC 26 220