ExxonMobil Escorene™ LD 723.28 Cast Ethylene Vinyl Acetate Copolymer

Category Polymer , Thermoplastic , Ethylene Vinyl Acetate
Manufacturer Exxon Chemical
Trade Name Escorene™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene™ LD 723.28 Cast Ethylene Vinyl Acetate Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Escorene Ultra UL 723.28 is a high VA extrusion coating resin, which provides outstanding heat sealability and high clarity. LD 723.28 has a good balance of drawabilty and neck-in and can be coextruded with LDPE extrusion coating resins on most coextrusion coating lines.Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: No Thermal Stabilizer: Yes Applications:Heat Seal LayerExtrusion CoatingInformation provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.939 g/cc
0.0339 lb/in³
ExxonMobil method
Vinyl Acetate Content 18.5 %
18.5 %
ExxonMobil method
Melt Flow 23 g/10 min

@Load 2.16 kg,
Temperature 190 °C
23 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 530 %
530 %
ASTM D882
Film Elongation at Break, TD 810 %
810 %
ASTM D882
Elmendorf Tear Strength MD 240 g
240 g
ASTM D1922
Elmendorf Tear Strength TD 330 g
330 g
ASTM D1922
Dart Drop Test 90.0 g
0.198 lb
ASTM D1709A
Film Tensile Strength at Break, MD 21.4 MPa
3100 psi
ASTM D882
Film Tensile Strength at Break, TD 15.2 MPa
2200 psi
ASTM D882
1% Secant Modulus, MD 51.0 MPa
7400 psi
ASTM D882
1% Secant Modulus, TD 55.2 MPa
8000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point <= 183 °C
<= 361 °F
Peak Melting Point; ExxonMobil method
Vicat Softening Point 53.9 °C
129 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 0.90 %
0.90 %
ASTM D1003
Gloss 89 %
89 %
45°; ASTM D2457